Glycerol known as by-product of transesterification of vegetables oil become an important materials after some chemical modification. In this study, hydrogenolysis reaction of glycerol to 1,2-propanediol was conducted using various supported ruthenium based catalyst. The support materials used in this study are bentonite ,TiO2, Al2O3 and SiO2. All experiments were carried out at reaction condition of 150°C, hydrogen pressure 20-30 bar for 7 hours and the 20%(wt) glycerol content in distilled water. The result shows that activity of the catalyts increased following this order: Ru/SiO2< Ru/TiO2 ˜ Ru/Al2O3 < Ru/bentonite. High selectivity to 1,2-propanediol was obtained in hydrogenolysis glycerol over Ru/TiO2 (83.7% ) and Ru/bentonite (80.1%) catalysts. Since Ru/bentonite catalyst performed better than other tested catalyst, we choose this catalyst system to investigate the effect of various solid acids (zeolite, ZrO2, Nb2O5 and amberlyst) on conversion of glycerol in hydrogenolysis reaction. Addition of solid acid in hydrogenolysis glycerol had promote the activity of Ru/bentonite catalyst drastically. The result shows that the presence of zeolite make the conversion of glycerol increased to maximum from 62.8% to 81.6% compared the other solid acids. Interestingly, selectivity to 1,2-propanediol still was achieved over 80.0%. These catalysts system were characterized by XRD, XPS, BET, and TEM for obtaining some physicochemical properties of the catalysts

Adnan, Nadia Farhana

Alias, Aznira

Hamzah, Noraini

Kassim, Mohamad

Mohamad Nordin, Norasikin

Nadzri, Ainol Hayah

Yarmo, Mohd. Ambar

Universiti Teknologi Malaysia Institutional Repository

Effect of solid acids in the conversion of glycerol over ru/bentonite catalyst in glycerol hydrogenolysis reaction Abstract Glycerol known as by-product of transesterification of vegetables oil become an important materials after some chemical modification. In this study, hydrogenolysis reaction of glycerol to 1,2-propanediol was conducted using various supported ruthenium based catalyst. The support materials used in this study are bentonite ,TiO2, Al2O3 and SiO2. All experiments were carried out at reaction condition of 150°C, hydrogen pressure 20-30 bar for 7 hours and the 20%(wt) glycerol content in distilled water. The result shows that activity of the catalyts increased following this order: Ru/SiO2< Ru/TiO2 ˜ Ru/Al2O3 < Ru/bentonite. High selectivity to 1,2-propanediol was obtained in hydrogenolysis glycerol over Ru/TiO2 (83.7% ) and Ru/bentonite (80.1%) catalysts. Since Ru/bentonite catalyst performed better than other tested catalyst, we choose this catalyst system to investigate the effect of various solid acids (zeolite, ZrO2, Nb2O5 and amberlyst) on conversion of glycerol in hydrogenolysis reaction. Addition of solid acid in hydrogenolysis glycerol had promote the activity of Ru/bentonite catalyst drastically. The result shows that the presence of zeolite make the conversion of glycerol increased to maximum from 62.8% to 81.6% compared the other solid acids. Interestingly, selectivity to 1,2-propanediol still was achieved over 80.0%. These catalysts system were characterized by XRD, XPS, BET, and TEM for obtaining some physicochemical properties of the catalysts. 

Effect of solid acids in the conversion of glycerol over ru/bentonite catalyst in glycerol hydrogenolysis reaction

Glycerol known as by-product of transesterification of vegetables oil become an important materials after some chemical modification. In this study, hydrogenolysis reaction of glycerol to 1,2-propanediol was conducted using various supported ruthenium based catalyst. The support materials used in this study are bentonite ,TiO2, Al2O3 and SiO2. All experiments were carried out at reaction condition of 150&deg;C, hydrogen pressure 20-30 bar for 7 hours and the 20%(wt) glycerol content in distilled water. The result shows that activity of the catalyts increased following this order: Ru/SiO2&lt; Ru/TiO2 &asymp; Ru/Al2O3 &lt; Ru/bentonite. High selectivity to 1,2-propanediol was obtained in hydrogenolysis glycerol over Ru/TiO2 (83.7% ) and Ru/bentonite (80.1%) catalysts. Since Ru/bentonite catalyst performed better than other tested catalyst, we choose this catalyst system to investigate the effect of various solid acids (zeolite, ZrO2, Nb2O5 and amberlyst) on conversion of glycerol in hydrogenolysis reaction. Addition of solid acid in hydrogenolysis glycerol had promote the activity of Ru/bentonite catalyst drastically. The result shows that the presence of zeolite make the conversion of glycerol increased to maximum from 62.8% to 81.6% compared the other solid acids. Interestingly, selectivity to 1,2-propanediol still was achieved over 80.0%. These catalysts system were characterized by XRD, XPS, BET, and TEM for obtaining some physicochemical properties of the catalysts

Yarmo, Mohd Ambar

Journals of Universiti Tun Hussein Onn Malaysia (UTHM)

59Journal of Science and TechnologyEffect Of Solid Acids In The Conversion Of Glycerol Over Ru/Bentonite  Catalyst In Glycerol Hydrogenolysis ReactionNoraini Hamzah1,2, Aznira Alias2, Nadia Farhana Adnan2, Ainol Hayah Nadzri2,Norasikin Mohamad Nordin3, Mohamad Kassim2, Mohd Ambar Yarmo21School of Chemical Sciences and Environmental , Faculty of Applied Sciences, University of Technology MARA2School of Chemical Sciences and Food Technology, Faculty of Science and Technology, Universiti Kebangsaan Malaysia 3Department of Science, UTM SPACE, Universiti Teknologi Malaysia International Campus*Corresponding email : norainihamzah@gmail.comAbstract Glycerol known as by-product of transesterification of vegetables oil become an important materials after some chemical modification. In this study, hydrogenolysis reaction of glycerol to 1,2-propanediol was conducted  using various supported ruthenium based catalyst. The support materials used in this study are bentonite ,TiO2, Al2O3 and SiO2. All experiments were carried out at reaction condition of 150°C, hydrogen pressure 20-30 bar for 7 hours and the 20%(wt) glycerol content in distilled water. The result shows that activity of the catalyts increased following this order: Ru/SiO2< Ru/TiO2 ≈ Ru/Al2O3 < Ru/bentonite. High selectivity to 1,2-propanediol was obtained in hydrogenolysis glycerol over Ru/TiO2 (83.7% ) and Ru/bentonite (80.1%) catalysts. Since Ru/bentonite catalyst performed better than other tested catalyst, we choose this catalyst system to investigate the effect  of various solid acids (zeolite, ZrO2, Nb2O5 and amberlyst) on conversion of glycerol in hydrogenolysis reaction. Addition of solid acid in hydrogenolysis glycerol had  promote the activity of Ru/bentonite catalyst drastically. The result shows that  the presence of zeolite make the conversion of  glycerol increased to maximum from 62.8% to 81.6% compared the other solid acids. Interestingly, selectivity to 1,2-propanediol still was achieved over 80.0%. These catalysts system were characterized by XRD, XPS, BET, and TEM for obtaining some physicochemical properties of the catalysts.Keywords : solid acid; glycerol; hydrogenolysis; ruthenium catalyst; bentonite60Journal of Science and Technology1 INTRODUCTIONTransesterification of triglycerides with methanol in the presence of basic or acidic catalysts produced biodiesel that consists of fatty acid methyl esters. Every 9 kg of biodiesel production, about 1 kg of crude glyderol by-product is also formed [1]. Nowadays, biodiesel derived from vegetable oils and animal fats has received considerable attention. The recent rapid development of biodiesel processes has caused some concern over the oversupply of glycerol in the glycerol market. The glycerol market will likely to be saturated because of limited utilization of glycerol at the present time [2]. Recently, catalytic conversion of glycerol to other value product via hydrogenolysis reaction has received considerable attention.  The hydrogenolysis of glycerol produces 1,2-propanediol (1,2-PDO) and ethylene glycol (EG) as a major products with a 4% annual market growth [3]. Typical uses of 1,2-propanediol are in production of unsaturated polyester resins, functional fluids, pharmaceuticals, cosmetics, paints, etc [4]. Therefore, the new usages of glycerol are being quested widely. Several groups have reported  on different catalyst systems, including supported transition metal catalyst such as Rh, Ni, Ru, Pt, Pt-Ru and Cu catalyst, for the hydrogenolysis of glycerol [5-13]. Previous study have been reported that among the metal catalysts, supported Ru catalyst was the most active for the hydrogenolysis of glycerol [14]. Previous research shows that hydrogenolysis of glycerol to propanediols proceed via dehydration of glycerol to acetol on acid catalysts and consecutive hydrogenation over metal catalysts. [15, 16]. Thus, a hydrogenolysis reaction is known as a bifuntional reaction. It requires catalysts both for dehydration and for hydrogenation functionality. According to the previous report, acid catalysts play an important role in hydrogenolysis reaction. Different solid acid catalysts such as zeolite, sulfated zirconia, tungstic acid and ion exchange resin have been studied as acid catalyst[17].    Best of our knowledge, there are a few reports using solid acid as co catalyst during glycerol hydrogenolysis over supported Ru catalyst, but there no study or report on Ru/bentonite catalyst system. Therefore, in the pres-ent  study  glycerol hydrogenolysis will carried out over Ru/bentonite using at different solid acid catalyst (zeolite, ZrO2, Nb2O5 and amberlyst) in order to investigate the effect of these solid acids  on its conversion and selectivity. 61Journal of Science and Technology2 EXPERIMENTAL2.1 Catalyst preparationGlycerol (99.9%) , ruthenium trichloride, RuCl3 were purchased from Sigma-Aldrich. The TiO2, bentonite, SiO2 and Al2O3 used as support were  obtained from Sigma-Aldrich also. The support materials were calcined in air at 500°C for 3 hours before used to remove moisture and impurities. All supported  catalysts with 5% metal loading were prepared by impregnation method. The precusor used for Ru was RuCl3 .  2.2  Catalyst characterization. The surface area of the supported metal catalyst was measured using the Brunauer-Emmett- Teller(BET) method (N2 adsorption) with a Gemini apparatus (Micromeritics 2010 Instrument Corporation). Transmission Electron Microscope (TEM) images were taken for determination of the particle size with a CM12 instrument (Philips) operated at 200 kV. The samples were dispered by supersonic waves in ethanol. Then they were placed on Cu grids under air atmosphere. General morphology information of the samples were examined by Field Emission Scanning Electron Microscope (FESEM) with LEO 1450VP model equipped with energy dispersive X-ray detector (EDX). All the samples were analysed in a high-vacuum mode at 20 kV. The phase structures of the catalysts were determined by X-Ray Diffraction (XRD) patterns using Bruker AXS D8 Advance  X-ray Powder Diffractometer with Cu Kα (λ= 0.15406 nm) at angle 2θ = 20 - 80. About 2.0 gram of sample was grinded and the fine powder was pressed on the holder of diffractometer. The X-ray photoelectron spectrum (XPS) data of the as-prepared samples were obtained with an XPS type ultra from kratos. Sample was analysed at 3 x 10-9 Torr. The binding energies were referenced to the C 1s line at 284.5 eV from adventitious carbon. This C 1s at 284.5 eV was used to calculate the different binding energy (ΔBE) between  C 1s peak in the samples. 2.3  Catalytic reaction and product analysis. The catalytic hydrogenolysis reactions were carried out in a 50 ml stainless-steel with teflon liner autoclave, PARR reactor equipped with an electronic temperature controller and a mechanical stirrer. Reaction was normally conducted under the following standard conditions : 150°C temperature, 20 bar initial hydrogen pressure, 1.0 g catalyst weight, 23 ml of 20 wt% aqueous solution of glycerol, 7 h reaction time and at constant striring speed at 200 rpm.62Journal of Science and Technology The hydrogenolysis reaction sequence was as follows: loading of the reactor with aqueous solution of glycerol and the approriate amount of catalyst. Then the reactor was flushed three times with N2 in order to remove oxygen gas  and pressurized with H2 to 20 bar. The mixture of glycerol and the catalyst was heated up to 150°C at constant stiring speed at 200 rpm and maintained for 7 hours. After the reaction, the reactor was cooled at room temperature and the liquid phase products were separated from the catalyst by centrifuge at 4000 rpm during 15 min then filtered. These products were analysed using a gas chromatograph (GC-Hewlett Packard Model 6890N) equipped with a flame ionization detector (FID). The gas chromatograph(GC) column used was a DB-WAX capillary column (30 m x 0.32 mm x 0.5 μm) manufactured by Angilent Technologies. Solutions of n-butanol and 1,4-butanediol with known amounts of internal standards were  used for quantification of various glycerol-derived compounds in the product.3 RESULTS AND DISCUSSION 3.1 Catalyst characterizationThe physico-chemical properties of the support material and 5%(wt) supported Ru catalysts used in this study are shown in Table 1. The BET specific surface area of support TiO2, bentonite, SiO2 and AlO3 were found to be 8.8 m2g-1,101.3 m2g-1,130.5 m2g-1 and 155.6 m2g-1 respectively. Analysis BET showed that support material namely bentonite, SiO2 and Al2O3 have similar BET surface area value in the range (100-150) m2/g except TiO2 has the lowest BET surface area value.Table 1 : Surface area of supports and supported catalystSupportBET Surface Area, m2/g Supported CatalystsBET surface area (m2/g)Bentonite 101.3 Ru/bentonite 35.4TiO2 8.8 Ru/TiO2 7.9SiO2 130.5 Ru/SiO2 125.3Al2O3 155.6 Ru/Al2O3 141.4 BET surface area of Ru/bentonite, Ru/TiO2, Ru/SiO2 and Ru/Al2O3 catalysts obtained are 35.4, 7.9, 125.3 and 141.4 m2/g respectively. BET analysis revealed that catalyst of Ru/SiO2 and 63Journal of Science and TechnologyRu/Al2O3 have similar surface area, meanwhile Ru/TiO2 has the smaller surface area. Previous study have claimed that the decrease in BET surface area value of the catalysts after 5% (wt) Ru loading is due to pore blockage of support by crystallites of Ru [14].  The series of these catalysts were characterized by XRD as shown in  Fig.1.  As we can seen, Ru supported on TiO2 have crystalline form whereas Ru supported on Al2O3, bentonite and SiO2 have amorphous phase. It seem that XRD pattern of Ru/bentonite shows weak diffraction peak at 2θ = 40.5° , 43.0° and 55.0° which could be assigned to RuO2 species. On the other hand, there are no characteristic peak related to metallic Ru was observed for  Ru/AlO3, Ru/SiO2 and Ru/TiO2. Previous study shows that the absence of peak Ru particles  at low content (5% metal loading) might be due to the presence of nano Ru particles ina highly dispersed on the supports [18] . Figure 1 : XRD pattern of Al2O3 and 5%(wt) Ru/AlO3(a), bentonite and 5%(wt) Ru/bentonite(b), TiO2 and 5%(wt) Ru/TiO2 (c), SiO2 and 5%(wt) Ru/SiO2 Since XRD pattern did not shows the peak related to Ru particle, therefore in order to study the existence of Ru element on the support, XPS analysis was done. Fig. 2 illustrate the XPS 64Journal of Science and Technologywide scan spectra of Ru/Al2O3(a), Ru/Bentonite(b), Ru/TiO2(c), Ru/SiO2(d). As we can see, wide scan spectra clearly shows the presence of Ru species on the supports. The presence of Ru species cause peak of Ru3d appear in the XPS spectra of each catalyst.   Figure 2 : XPS spectra wide scan spectrum of Ru/Al2O3(a), Ru/Bentonite(b), Ru/TiO2(c),  Ru/SiO2(d) Chemical state of the Ru element was investigate  via narrow scan  and the spectra are shown in Fig.3. Since the binding energy (B.E) of Ru 3d5/2 (280 eV) overlapped with that C 1s (284.5 eV), it was difficult to resolve the small Ru peak out from the large peak of C 1s. The Ru 3d spectra revealed the presence of two different chemical state on the surface ( Ru0 at 281.0 eV and Ru4+ at 283.3 eV) except Ru species on bentonite shows chemical state of  Ru0 species only. Previous study have found that B.E of ≈ 283.0 eV was assigned to RuO2 which is corresponding to Ru4+ species.[14] Meanwhile according Balaraju et al. to the B.E value of Ru0 species was in the range 280- 281 eV.[14]  The presence of Ru4+ species indicated the Ru exists as oxide form  and this species might be form during calcinations process.         65Journal of Science and TechnologyFigure 3 : XPS spectra of narrow scan of the Ru region for Ru/Al2O3(a) , Ru/bentonite (b), Ru/TiO2(c)  and Ru/SiO2(d)  FESEM-EDX analysis was done to investigate further the dispersion of Ru particles and it seems that Ru particle is more dispersed on bentonite support and this result was related with catalytic activity of Ru catalyst. Fig. 4 illustrated the morphology of the catalyst analyze by TEM and the average size particle measured by TEM of Ru particle on bentonite, Al2O3, SiO2 and TiO2 were ≈ 1.5 nm, < 2nm, ≈ 2 nm and 4-6 nm. This result indicate that size particles of Ru were much smaller on bentonite support than others support. 66Journal of Science and TechnologyFigure 4 : TEM image of Ru/Al2O3(a), Ru/Bentonite(b), Ru/TiO2(c),  Ru/SiO2(d)3.2 Hydrogenolysis glycerolThe effect of support materials on catalytic of behavior of Ru catalyst for hydrogenolysis glycerol was investigated under mild reaction condition of 150°C, 20 bar initial hydrogen pressure for 7 hours reaction time. The concentration of glycerol  in distilled water was 20%(wt). Table 1 summarized the activities of glycerol hydrogenolysis over Ru metal catalyst supported on bentonite, TiO2, Al2O3 and SiO2. The result shows that Ru/bentonite exhibited the most active (62.8%) in hyrogenolysis glycerol meanwhile Ru/TiO2 gave the highest selectivity (84.4%) to 1,2-propanediol. The result also revealed that all the catalysts gave same selectivity to EG.  From the results , it is clear that these catalysts were favour to C-O breaking bond compared to C-C bond. Therefore, product 1,2-propanediol considered as a main product in hydrogenolysis glycerol using this system catalyst. The activity of the catalyst was not related with high surface area, since Ru/bentonite catalyst did not possess the highest surface area. The BET surface area value 67Journal of Science and Technologyfollowing this: Ru/Al2O3 > Ru/SiO2 > Ru/bentonite > Ru/TiO2. This result also implies that glycerol conversion greatly depend on the nature of the support. Previous study was found that solid base (hydrotalcite and MgO) supported Pt catalysts exhibited the predominant activity and higher 1,2-propanediol selectivity than of solid acids (Al2O3, H-ZSM5 and H-Beta) [19]. In our case, bentonite which is base material support shows better catalytic performance and this result was quite similar with previous report.Table 1: Glycerol hydrogenolysis over supported Ru catalysts.Catalyst Glycerol conversion(%)Selectivity (%)1,2-PDO EGRu/bentonite 62.8 80.1 9.9Ru/TiO2 38.8 84.4 11.2Ru/Al2O3 38.9 71.0 12.7Ru/SiO2 15.6 76.3 7.0Reaction conditions: 20 (wt%) glycerol in water, H2 pressure = 20-30 bars, reaction time = 7 hrs Since Ru/bentonite catalyst performed better among the tested catalyst, so we choose this catalyst for further investigation. Different solid acid catalyst as co-catalyst are added in  Ru/bentonite catalyst during glycerol hydrogenolysis reaction and the results are shown in Table 2. It was found that activity of Ru/bentonite increased when using solid acid as the additive/co-catalyst. The order of activity for the solid acid catalysts are as follow: zeolite > ZrO2 > Nb2O5 > Amberlyst. The result revealed that the highest activity of the catalyst obtained when zeolite was used as solid acid. Interestingly the selectivity towards 1,2-propanediol was also high. Previous studied have reported that activity of the catalyst was high when Amberlyst is used as the solid acid catalyst and they also found that Amberlyst decomposes under reaction condition more than 120°C  [17]. Similar result was obtained in this study since activity of the Amberlyst catalyst exhibited the lowest activity.68Journal of Science and TechnologyTable 2 : Influence of solid acid as co-catalyst in the hydrogenolysis of glycerol reaction over Ru/Bentonite catalystMetal catalyst Acid catalyst Conversion(%)Selectivity (%)1,2-PD EGRu/bentonite - 62.8 80.1 9.9Ru/bentonite zeolite 81.6 81.5 8.5Ru/bentonite ZrO2 77.6 77.7 10.0Ru/bentonite Nb2O5 75.5 83.6 11.4Ru/bentonite Amberlyst 69.4 8.0 -Reaction conditions: 20 (wt%) glycerol in water, H2 pressure = 20-30 bars, reaction time = 7 hrs4 CONCLUSIONSThe solid acid as a co-catalyst influences the conversion of glycerol during hydrogenolysis over Ru/bentonite. This study indiates that the catalyst activity greatly depend on the types of solid acid used during the hydrogenolysis reaction. Among different solid acid catalysts studied, zeolite exhibited better activity. Further research have to be carried out in order to study the amount of acid site  and the synergistic effect towards glycerol conversion and selectivity to 1,2-propanediol.ACKNOWLEDGEMENTSThe authors would like to acknowledge Universiti Teknologi MARA(UiTM) for fundings staff schlorships and all members lab catalysis, UKM. The authors also would like to thanks  CRIM, UKM for instrument such as XPS, TEM and FESEM and all lab assistant, espcecially En Adnan,  Puan Suhaiza, En Zaki, En Haznor for their contributing in this research.  This study was funded by grant FRGS /1/10/ST/UKM/01/7.REFERENCES[1] E.S. Vasiliadou, E. Heracleous, I.A. Vasalos and A.A. Lemonidou:   Applied Catalysis B: Environmental  Vol. 1-2  (2009), p. 90-99.[2] J. Feng, H. Fu, J. Wang, R. Li, H. Chen and X. Li: Catalysis    Communications  Vol. 6  (2008), p. 1458-1464.69Journal of Science and Technology[3] J. Chaminand, L.A. Djakovitch, P. Gallezot, P. Marion, C. Pinel and   C. Rosier: Green Chemistry  Vol. 8  (2004), p. 359-361.[4] E.P. Maris and R.J. Davis: Journal of Catalysis  Vol. 2  (2007), p.   328-337.[5] Y. Shinmi, S. Koso, T. Kubota, Y. Nakagawa and K. Tomishige:    Applied Catalysis B: Environmental  Vol. 3-4  (2010), p. 318-326.[6] J. Wang, S. Shen, B. Li, H. Lin and Y. Yuan: Chemistry Letters  Vol.   6  (2009), p. 572-573.[7] Z. Yuan, P. Wu, J. Gao, X. Lu, Z. Hou and X. Zheng: Catalysis    Letters  Vol. 1-2  (2009), p. 261-265.[8] J. Zheng, W.C. Zhu, C.X. Ma, M.J. Jia, Z.L. Wang, Y.H. Hou and   W.X. Zhang: Polish Journal of Chemistry  Vol. 7  (2009), p. 1379-  1387.[9] J.H. Zhou, M.G. Zhang, L. Zhao, P. Li, X.G. Zhou and W.K. Yuan:   Catalysis Today  Vol. SUPPL.  (2009), p. S225-S229.[10] A. Bienholz, F. Schwab and P. Claus: Green Chemistry  Vol. 2     (2010), p. 290-295.[11] T. Kurosaka, H. Maruyama, I. Naribayashi and Y. Sasaki: Catalysis   Communications  Vol. 6  (2008), p. 1360-1363.[12] C. Montassier, J.C. Ménézo, J. Moukolo, J. Naja, L.C. Hoang, J.    Barbier and J.P. Boitiaux: Journal of Molecular Catalysis  Vol. 1    (1991), p. 65-84.[13] U. Saxena, N. Dwivedi and S.R. Vidyarthi: Industrial and    Engineering Chemistry Research  Vol. 5  (2005), p. 1466-1473.[14] M. Balaraju, V. Rekha, B.L.A.P. Devi, R.B.N. Prasad, P.S.S. Prasad   and N. Lingaiah: Applied Catalysis A: General  Vol. 384  (2010), p.   107-114.[15] Erin P. Maris a, William C. Ketchie a, Mitsuhiro Murayama b and   Robert J. Davis a: Journal of Catalysis Vol. (2007), p. 281-294.70Journal of Science and Technology[16] T. Miyazawa, Y. Kusunoki, K. Kunimori and K. Tomishige: Journal   of Catalysis  Vol. 2  (2006), p. 213-221.[17] Y. Kusunoki, T. Miyazawa, K. Kunimori and K. Tomishige: Catalysis   Communications  Vol. 10  (2005), p. 645-649.[18] S. Bolado, R.E. Treviño, M.T. García-Cubero and G.G. Benito:    Catalysis Communications  Vol. 2  (2010), p. 122-126.[19] Z. Yuan, J. Wang, L. Wang, W. Xie, P. Chen, Z. Hou and X. Zheng:  Bioresource Technology  Vol. (2010), p.

English

Effect Of Solid Acids In The Conversion Of Glycerol Over Ru/Bentonite Catalyst In Glycerol Hydrogenolysis Reaction

https://publisher.uthm.edu.my/ojs/index.php/JST/article/download/246/125

Effect of solid acids in the conversion of glycerol over ru/bentonite catalyst in glycerol hydrogenolysis reaction

Abstract

Similar works

Full text

Available Versions

Universiti Teknologi Malaysia Institutional Repository

Journals of Universiti Tun Hussein Onn Malaysia (UTHM)