Water vapor is condensed onto a cold sample, coating it with a thin-film of ice. The ice is sensitive to electron beam lithography exposure. 10 nm ice patterns are transferred into metals by “melt-off”. Non-planar samples are coated with ice, and we pattern on cantilevers, AFM tips, and suspended nanotubes

Online Research Database In Technology

                       General rights Copyright and moral rights for the publications made accessible in the public portal are retained by the authors and/or other copyright owners and it is a condition of accessing publications that users recognise and abide by the legal requirements associated with these rights.  • Users may download and print one copy of any publication from the public portal for the purpose of private study or research. • You may not further distribute the material or use it for any profit-making activity or commercial gain • You may freely distribute the URL identifying the publication in the public portal   If you believe that this document breaches copyright please contact us providing details, and we will remove access to the work immediately and investigate your claim.     Downloaded from orbit.dtu.dk on: Nov 08, 2017Ice Lithography for NanodevicesHan, Anpan; Kuan, A.; Wang, J.; Vlassarev, D.; Golovchenko, J.; Branton, D.; Tiddi, William; Beleggia,MarcoPublication date:2015Document VersionPublisher's PDF, also known as Version of recordLink back to DTU OrbitCitation (APA):Han, A., Kuan, A., Wang, J., Vlassarev, D., Golovchenko, J., Branton, D., ... Beleggia, M. (2015). IceLithography for Nanodevices. Abstract from 5th Conference on Advances in Optoelectronics and Micro/Nano-optics, Hangzhou, China.The 5th Conference on Advances in Optoelectronics and Micro/Nano-optics (AOM 2015), Hangzhou, China Ice Lithography for Nanodevices A. Han1, A. Kuan4, J. Wang3,6, D. Vlassarev3,7, J. Golovchenko3,4, D. Branton5 W. Tiddi1, M. Beleggia2 1Danchip, 2CEN, Technical University of Denmark, Kgs. Lyngby, 2880, Denmark, anph@dtu.dk 3Dept. Physics, 4SEAS,  5Dept. Mole. and Cell. Bio., Harvard, Cambridge, Mass 02188., United States 6Dept. Applied Physics, Stanford University, Stanford, CA 94305, United States  7 Seagate Technologies, Longmont, CO 80503, United States  Abstract. Water vapor is condensed onto a cold sample, coating it with a thin-film of ice. The ice is sensitive to electron beam lithography exposure. 10 nm ice patterns are transferred into metals by “melt-off”. Non-planar samples are coated with ice, and we pattern on cantilevers, AFM tips, and suspended nanotubes.   The Harvard Nanopore Group is one of the pioneers in nanopore DNA sequencing [1]. For solid-state nanopore DNA sequencing, we needed to fabricate a chip with a  carbon nanotube field effect transistor traversing a nanopore. Originating from electron beam lithography PMMA resist, organic contamination a few nanometers thick, also called scum, partially bury nanotubes and clogs the nanopore just a few nanometers in diameter. While oxygen plasma is effective in removing scum, it also destroys the nanotubes. We discovered that it is possible to pattern ice with electron beam lithography (EBL), and named the method "ice lithography" [2]. Here, the main advantage is that water does not contaminate like organic resists. Fig. 1 illustrates ice lithography for patterning the electrodes of a nanotube field effect transistor. We modified a scanning electron microscope (SEM) for dedicated ice lithography [3]. In brief, we added a load lock for sample loading into the SEM vacuum chamber; a gas injection system to inject water vapor into the SEM vacuum chamber; a cryogenic system to cool the sample and condense water vapor from the GIS; a pattern generation system to guide the electron beam for writing in ice; and a metal deposition system for sputtering metals onto samples with ice patterns. After metal coating, the sample is unloaded from the instrument and immersed into isopropanol for “melt-off”. The ice melts, metal covering the ice is removed from the sample, while metal in patterned areas with no ice remains.  Unlike uniformly spinning resists that require a planar substrate, we can condense water vapor on non-planar surfaces and fragile samples and subsequently pattern [4]. We took advantage of this unique property to pattern on silicon nitride and oxide membranes down to 20-nm-thin. Because thin membranes are transparent to 200 keV electrons, it is possible to image metal patterns made by ice lithography by transmission electron microscopy (TEM). The smallest patterns are less than 10 nm (Fig 2a). The line edge roughness is so small that it is hardly measurable in the TEM images.  Using the same approach, we patterned on cantilevers and the apex of atomic force microscope probes tips. Such samples do not allow resist spin and bake.  To further test ice lithography for fragile and none planar samples, we patterned on suspended single walled carbon nanotube 5 nm in diameter and 1000 nm long. We coated the nanotube with 20 nm of ice film, then segments of ice along the nanotube were removed. Each segment was 25 nm wide, and the distance between segments was 150 nm. 5 Å of Ti was deposited over the entire sample, and by melt-off we made segment of Ti. Upon exposure to air, Ti forms TiO2, which seeds the growth of alumina by atomic layer deposition. We formed pearls (alumina particles) on a string (nanotube) structure (Fig 2b). We also made metal contacts to carbon nanotube for field effect transistors, with resulting electrical properties similar to contacts made by organic EBL resists [5]. We showed that ice lithography could be uniquely applied to make pristine carbon nanotube field effect transistors, and pattern on fragile samples with non-planar geometries, and hence enables the construction of a new generation of nanostructures with versatile functionalities. Ice lithography, however, has some drawbacks: the exposure dose is 1000 times higher than PMMA. For our work, less than 30 minutes is dedicated to ice resist exposure, and we save time because all processes are done using the ice lithography instrument. While it is clearly not yet suitable for production of semiconductor devices, we believe ice lithography has unique advantages in a research perspective. At the The 5th Conference on Advances in Optoelectronics and Micro/Nano-optics (AOM 2015), Hangzhou, China National Micro and Nanofabrication facility DTU Danchip we are setting up an new ice lithography instrument, and at the DTU core electron microscopy facility DTU Cen, we will study electron ice interactions, which is an exciting and unexplored area.  Acknowledgements Supported by grant R01HG003703 from the National Human Genome Research Institute, NIH to J.G. and D.B. We thank Dr. Hoogerheide for assistance in TEM A.H. thank the Carlsberg Foundation with a postdoctoral grant. [1] D. Branton, et al., “The potential and challenges of nanopore sequencing,” Nat. Biotechnol., vol. 26, no. 10, pp. 1146–1153, 2008. [2] G. M. King, G. Schurmann, D. Branton, and J. Golovchenko, “Nanometer Patterning with Ice,” Nano Lett., vol. 5, pp. 1157–1160, 2005. [3] A. Han, J. Chervinsky, D. Branton, and J. A. Golovchenko, “An ice lithography instrument,” Rev. Sci. Instrum., vol. 82, no. 6, 2011. [4] A. Han, A. Kuan, J. Golovchenko, and D. Branton, “Nanopatterning on nonplanar and fragile substrates with ice resists,” Nano Lett., vol. 12, no. 2, pp. 1018–1021, 2012. [5] A. Han, D. Vlassarev, J. Wang, J. A. Golovchenko, and D. Branton, “Ice lithography for nanodevices,” Nano Lett., vol. 10, no. 12, pp. 5056–5059, 2010.   Figure 1. Ice lithography process illustration  Figure 2. (a) TEM image of Pd structures on 50-nm-thin silicon nitride film, and nanoparticles on nanotubes (b).  Anpan Han: Niels Bohr Institute, Uni. Copenhagen, Denmark. PhD in Micro and Nanotechnology from Uni.  Neuchâtel, Switzerland (2006). Post-doc at Harvard Uni., USA. Now Assistant Prof. Danchip, Technical Uni. of Denmark. Research focus is micro and  nanofabrication technologies including instrumentation, materials, characterization, process flow and optimization. Fabrication technologies are electron beam lithography, DUV and UV lithography, DRIE, RIE, Ion milling, ALD, PVD, PECVD,  LPCVD. Characterization: SEM, FIB, TEM, AFM, XPS, ellipsometry. Materials: metals, polymers, silicon, diamond.     

Ice Lithography for Nanodevices

http://orbit.dtu.dk/ws/files/118743876/AOM_2015_Abstract_Anpan_Han_1.pdf

Ice Lithography for Nanodevices

Abstract

Similar works

Full text

Available Versions

Online Research Database In Technology