This is the accepted version of the following article: Cherrington, R., Hughes, D. J., Senthilarasu, S. and Goodship, V. (2015), Inkjet-Printed TiO2 Nanoparticles from Aqueous Solutions for Dye-Sensitized Solar Cells (DSSCs). Energy Technology., which has been published in final form at http://dx.doi.org/10.1002/ente.201500096This work reports on the formulation of suitable ink for inkjet printing of TiO2 by investigating the critical parame- ters of particle size, pH, viscosity, and stability. Aqueous sus- pensions of TiO2 nanoparticles (Degussa, P25) were pre- pared with the addition of 25 wt % polyethylene glycol 400 as a humectant to minimize drying at the printer nozzles and reduce the likelihood of nozzle blockage. The inkjet-printed TiO2 layers were assembled into dye-sensitized solar cells. The current–voltage (I–V) characteristics were measured under one sun (air mass 1.5, 100 mW cm 2) using a source meter (Model 2400, Keithley Instrument, Inc.), and the active area of the cell was 0.25 cm2. The inkjet-printed TiO2 photoanode produced a device with a short-circuit current (Isc) of 9.42 mA cm 2, an open-circuit voltage (Voc) of 0.76 V, and a fill factor (FF) of 0.49, resulting in a power conversion efficiency (PCE) of 3.50 %.Engineering and Physical Sciences Research Council (EPSRC