Thermoplastic natural rubber (TPNR) composite was prepared using melt blending method. The TPNR composites have been made with carbon fibers with random planar orientation both with treated and untreated with 1M sulfuric acid. The effect of surface treatment on the carbon fibre, strain rate

and temperature on mechanical properties of the composites at various fibre loading (10%-40%) was investigated. It was found that the tensile properties of surface treated carbon fibre TPNR composite increased linearly with fiber

concentration and decreased as temperature increased. The tensile stress also increased linearly with strain rate from 10-3 to 10-1 S-I. SEM micrograph on the

fractured surface has shown that the sulfuric treated fibre had improved the fiber-matrix adhesion of TPN

Ahmad, Sahrim

Mohamed, Nor Hasimah

Universiti Putra Malaysia Institutional Repository

Pertanika J. Sci. & Techno!. 8(2): 117-124 (2000)ISSN: 0128-7680© Universiti Putra Malaysia PressKesan SOOu dan Kadar Terikan ke atas Sifat ReganganKomposit Getah Asli Tennoplastik (HDPE/NR)Berpenguat Gentian Karbon PendekSahrim Hj. Ahmad dan Nor Hasimah MohamedProgram Sains BahanFakulti Sains Fizis dan GunaanUniversiti Kebangsaan Malaysia43600 Bangi, Selangor Darul Ehsan, MalaysiaReceived: 19 Julai 1999ABSTRAKKomposit getah asli termoplastik (TPNR) berpenguat gentian karbon denganarah orientasi rawak telah dihasilkan dengan kaedah pengadunan leburanmenggunakan gentian yang dirawat dengan asid sulfurik dan gentian tanparawatan. Kesan rawatan permukaan gentian, kadar terikan dan suhu terhadapsifat mekanik komposit TPNR dikaji pada pelbagai komposisi gentian (10% -40%). Keputusan menunjukkan kekuatan regangan meningkat denganpenambahan gentian. Didapati kekuatan regangan juga meningkat dengankadar terikan dari 10-3 hingga 10-1 S-I dan menurun dengan peningkatan suhupersekitaran. Keputusan juga menunjukkan bahawa sifat mekanik kompositTPNR dengan gentian yang dirawat meningkat dengan peningkatan komposisigentian berbanding dengan gentian tanpa rawatan. Mikrograf MikroskopImbasan Elektron (SEM) pada permukaan patah pula jelas menunjukkanterdapatnya pelekatan yang baik antara gentian dan matrik pada kompositTPNR yang dirawat asid sulfurik.Kata kunci: getah asii termoplastik, komposit TPNR, gentian karbon, rawatanpermukaanABSTRACfThermoplastic natural rubber (TPNR) composite was prepared using meltblending method. The TPNR composites have been made with carbon fiberswith random planar orientation both with treated and untreated with 1Msulfuric acid. The effect of surface treatment on the carbon fibre, strain rateand temperature on mechanical properties of the composites at various fibreloading (10%-40%) was investigated. It was found that the tensile properties ofsurface treated carbon fibre TPNR composite increased linearly with fiberconcentration and decreased as temperature increased. The tensile stress alsoincreased linearly with strain rate from 10-3 to 10-1 S-I. SEM micrograph on thefractured surface has shown that the sulfuric treated fibre had improved thefiber-matrix adhesion of TPNR.Keywords: Thermoplastic natural rubber, TPNR composites, carbon fibre,surface treatmentSahrim Hj. Ahmad dan Nor Hasimah MohamedPENGENALANSifat mekanik polimer dan komposit dipengaruhi oleh pelbagai faktor sepertikadar terikan dan suhu (Agbossu et ai. 1994 & Hartingsveldt et ai. 1991). Sifatkomposit bergentian pendek dipengaruhi oleh antara muka gentian dan matrik.Big (1987) mendapati bahan penguat dalam bentuk gentian pendek dapatmeningkat sifat mekanik sesuatu polimer kerana kebolehannya menahan bebantegasan yang dipindahkan daripada matrik polimer (Figueiredo et al. 1990).Kajian lepas (Krekel 1994) yang melibatkan rawatan asid-bes menunjukkanterhasilnya lekatan yang baik antara gentian dan matrik kerana ia dapatmeningkatkan kekasaran gentian karbon dan seterusnya memperbaiki modkegagalan (Donnet & Ehrburger 1977). Rawatan permukaan secara pengoksidaanakan menambahkan kumpulan berfungsi pada gentian dan seterusnyameningkatkan ketegaran di kawasan antara muka (Figueiredo et at. 1990).Kumpulan berfungsi seperti - COOH memberikan sumbangan pelekatan yangtertinggi pada permukaaan karbon (Krekel et al. 1993). Kekuatan lekatanmelalui kumpulan berfungsi ini meningkat dengan peningkatan atom oksigen(Sawada et at. 1993).Kajian tentang kesan suhu dan kadar terikan bagi kestabilan sifat mekanikadalah penting terutamanya untuk penggunaan dalam struktur komposit (Wu1991). Gentian karbon tidak terjejas pada suhu kurang daripada 200·C.Sebaliknya kebanyakan bahan termoplastik akan mengalami perubahan rapuh-kenyal pada suhu yang agak tinggi yang dikenali sebagai suhu peralihan kaca,T (Cowley et at. 1997). Keadaan ini menjelaskan bahawa matrik polimerb~rgantung kepada suhu, dengan perubahan secara dramatik apabilamenghampiri suhu peralihan kaca T . Modulus Young dan tegasan putus dalamkajian Nicolais et at. (1971) didapaJ berkurangan dengan peningkatan suhu.Pada kawasan suhu ini, sifat kelikatan bahan meningkat dan tindak balasmekanik polimer lebih bergantung pada kadar terikan (Detassis et at. 1995).Dengan demikian modulus Young dan kekuatan alah secara umumnyabergantung kepada kadar ujian yang digunakan (Hartingsveldt et al. 1991).Kertas ini membincangkan kesan rawatan asid, kadar terikan dan suhu keatas komposit bergentian karbon pendek yang dirawat dengan asid sulfurik.KAEDAHBahan-bahanGetah asli (NR) jenis SMR-L dibekalkan oleh Guthrie (M) Bhd.; Cecair getahasli (LNR) disediakan secara fotooksidaan olehJabatan Kimia, UKM; Polietilenaberketumpatan tinggi (HDPE) jenis HMA-016 berketumpatan 0.956 gcm,3dikeluarkan oleh Mobil (M) Sdn. Bhd; Gentian karbon daripada jenis PANdibekalkan oleh Toray, dengan ± 6 mm panjang; Asid sulfurik berkepekatan95-97% dibekalkan oleh Merck; Asid nitrik berkepekatan 69-71 % dibekalkanoleh Fischer Inorganic, dan natrium hidroksida dibekalkan oleh HamburgChemicals dalam bentuk hablur.118 PertanikaJ. Sci. & Technol. Vol. 8 No.2. 2000Kesan Suhu dan Kadar Terikan ke atas Sifat Regangan Komposit Getah AsH TermoplastikRawatan Gentian KarbonGentian dibasuh menggunakan air suling dan dikeringkan pada suhu llO·Cselama duajam. Asid sulfurik (1M) dipanaskan sebanyak 300 ml sehingga suhumencapai 100·C. Se1epas itu gentian seberat 30g direndam ke dalam asidsulfurik selama 1 jam. Gentian tersebut kemudiannya dibasuh denganmenggunakan 1M NaOH dan direflukskan dengan 1M NaOH selama 1 jam.Gentian dikeluarkan dan diekstrakkan dengan air suling dalam ke1alang isipaduse1ama 5 hari. Gentian yang te1ah bersih dikeringkan pada suhu ambien (27·C)selama 2 hari sebe1um digunakan.Penyediaan Matrik TPNRNR/HDPE diadun menggunakan Brabender PL 2000 dengan komposisi 60/40menggunakan 10% LNR sebagai pengserasi. Adunan ini dilakukan pada suhu135·C dengan kadar putaran 30 rpm se1ama 15 minit. Matriks TPNR kemudiandikisar dengan Refec Granulator PL 300S meqiadi butiran halus.Penyediaan Komposit TPNRGentian karbon terawat dan matrik TPNR dimasukkan ke dalam mesin pemutarBrabender dengan komposisi gentian (10%-40%) pada suhu 135·C dan kelajuan11 rpm selama 11 minit.Pencirian BahanKekuatan regangan diukur dengan menggunakan alat Universaljenis Uyod PL2000 buatan Sintech mengikut prosedur piawai ASTM D412 pada ke1ajuan 50mm/min, 100mm/min, 500mm/min dan 900mm/min bagi sampel berbentuk"dumbell". Kekuatan hentaman diukur dengan menggunakan mesin banduldigital Universal Fractoscope berjenama Ceast 6545/000 mengikut prosedurpiawai ASTM D256-88. Morfologi permukaan patah dikaji menggunakanMikroskop Imbasan Elektron model XL 30 berjenama Philips.KEPUTUSAN DAN PERBINCANGANRajah 1 menunjukkan penambahan komposisi gentian sehingga 20%meningkatkan nilai tegasan maksimum komposit TPNR dan mengalamipenurunan pada komposisi 30% dan 40%. Nilai tegasan adalah lebih tinggipada komposit dengan gentian yang dirawat dengan asid sulfurik berbandingkomposit dengan gentian tanpa rawatan. Keadaan ini terjadi kerana terdapatlekatan yang baik antara matrik TPNR dan gentian yang disebabkan wujudnyamekanisme ikatan kimia dan daya-daya tarikan (Figueiredo et at. 1990) olehkumpulan berfungsi. Kumpulan berfungsi -OH pada permukaan gentian karbonterjana akibat rawatan asid sulfurik (Nakanishi et at. 1994). Pada komposisi yanglebih tinggi pula padatan gentian yang rapat menyebabkan matrik tidak dapatmeresap di an tara gentian dan seterusnya mengakibatkan kurangkeberkesanannya terhadap bebanan (Karan 1991).PertanikaJ. Sci. & Techno!. Vol. 8 No.2. 2000 119Sahrim Hj. Ahmad dan or Hasimah Mohamed35..-----------------,l'l6I QRa\-..OT.... R8q"11111Rajah 1 : Histogram tegasan maksimummelawan komposisi gentianRajah 2 : Histogram modulus Youngmelawan komposisi gentianDaripada pemerhatian pada Rajah 2 didapati penambahan gentianmeningkatkan modulus Young. Peningkatan modulus Young ini adalah menepatiteori penguat yang dicadangkan oleh Kerner (Nicolais et al. 1971). Nilaimodulus Young komposit didapati meningkat dengan peratus gentian sehingga20%. Peningkatan ini adalah didapati lebih tinggi pada komposit dengangentian yang dirawat. Tetapi apabila nilai peratus gentian melebihi 20%,modulus Young komposit jatuh dengan ketara terutamanya bagi kompositdengan gentian yang dirawat. Keadaan ini berlaku kerana kekuatan regangangentian berkurang apabila rawatan dilakukan ke atasnya (Wu et al. 1995). Olehitu penambahan gentian yang dirawat melebihi 20% menyebabkan kompositmudah mengalami kegagalan apabila bebanan dikenakan kerana kecacatanpermukaan yang dihasilkan.Rajah 3 menunjukkan plot tegasan alah melawan kadar terikan. Daripadarajah tersebut didapati tegasan alah meningkat hampir linear dengan kadarterikan. Ini adalah sesuai dengan teori Eyring.12"2 10C>.~0 80.:!!.eb 6.g<: 4a~" 2I-00.006 0.03-+-\OO/OVf___ 200/0Vf-'-300/0Vf0.06Kadar Terikan (S·I)0.6120Rajah 3: OraJ tegasan maksimum melawan kadar terikan pada suhu bilikPertanikaJ. Sci. & Techno!. Vo!. 8 0.2,2000Kesan Suhu dan Kadar Terikan ke atas Sifat Regangan Komposit Getah AsH TermoplastikRajah 4 menunjukkan tegasan maksimum juga meningkat denganpeningkatan kadar terikan yang dikenakan ke atas semua komposisi gentian.Pada kadar terikan yang rendah berlaku mekanisma canggaan yang disebabkanoleh proses terma. Mekanisma ini adalah dikawal oleh canggaan pada matrikdan tegasan akibat kehadiran gentian dan kumin hablur di dalam matrik(Agbossou et ai., 1994). Oleh itu kegagalan berlaku dengan mudah pada kadarterikan yang rendah. Menurut Abbossou et ai. (1994), kadar terikan yang tinggidikaitkan melalui model mekanik spring yang mengikuti hukum kelikatanNewton. Oleh itu mekanisma canggaan pada kadar terikan yang tinggi adalahberbeza daripada proses terma teraktif. Kajian yang dilakukan oleh Briscoe et ai.(1985) menunjukkan tiada peningkatan di dalam aliran tegasan pada kadarterikan yang tinggi.6~0-2 50c>;:tI., 4JE 3::lE ~----] -+-IO%Vf'"22 _20%Vfc-'-30%Vf'"~OIl'"f- 00.006 0.03 0.06 0.6Kadar Terikan (S·I)Rajah 4: Gra! modulus Young melawan kadar terikan pada suhu bilik4.5----'"Q.. 4.0~0 3.5ci;:tI., 3.0Eb 2.5E;:! 2.0c'".:o.t. 1.5'"~c 1.0'"'"'" 0.5OIlIlJf-0.030 50 70--IO%Vf ll'--20%Vf-A-30%Vfl90Suhu (DC)Rajah 5: Gra! tegasan maksimum melawan suhuPertanikaJ. Sci. & Techno!. Vo!. 8 No.2, 2000 121Sahrim Hj. Ahmad dan or Hasimah MohamedRajah 5 menunjukkan tegasan maksimum menurun apabila suhupersekitaran ditingkatkan daripada 30·C ke 90·C. ilai tegasan ini didapatilebih tinggi pada komposisi dengan gentian 20%. Disebabkan matrik TP Rmengalami canggaan apabila menghampiri suhu lebur Tm' iaitu pada suhu yang30.. 25p..~~ 20U.loil 15t:"0>-'"10":;-g 5~030 50 70-10O/OVf-+-200/0Vf-300/0Vf90Rajah 6: Oraf modulus Young melawan suhu(a) Suhu 50·C (b) Suhu 70·C122(c) Suhu 90·CRajah 7: Mikrograf SEM komposit TPNR berpenguat gentian karbon pendek padakomposisi gentian 20% pada pembesaran 500 XPertanikaJ. Sci. & Techno!. Vo!. 8 0.2,2000Kesan Suhu dan Kadar Terikan ke atas Sifat Regangan Komposit Getah AsH Termoplastiklebih tinggi terutamanya pada suhu 90·C, maka ini mengakibatkan lekatanantara gentian dan matrik menjadi lemah. Pada ketika ini daya penarikankeluar gentian daripada matrik dikurangkan (Cowley et at. 1997). Oleh yangdemikian, didapati modulus Young komposit jatuh dengan ketara pada 90·Ckerana kegagalan pada antara muka yang serius (Rajah 6). Corak penurunannilai ini dapat diterangkan dengan mikrograf mikroskop imbasan elektron(SEM) pada Rajah 7 yang diperolehi dari komposit bergentian 20%. Rajah 7menunjukkan gentian adalah melekat dengan kuat pada suhu 50·C.KESIMPULANKajian menunjukkan sifat mekanik komposit TPNR menggunakan rawatanpengoksidaan secara pembasahan asid sulfurik ke atas gentian karbon pendekberjaya ditingkatkan. Kekuatan regangan komposit didapati meningkat dengankadar terikan dan menurun dengan peningkatan suhu. Mikrograf SEMpermukaan patah menunjukkan lekatan yang kuat di antara gentian dan matrikTPNR pada suhu 50·C.PENGHARGAANPenulis mengucapkan terima kasih kepada UKM dan kerajaan Malaysia melaluimekanisme IRPA 03-02-02-0007 dan IRPA 09-02-02-0074 kerana bantuankewangan dan Che Moh Wan bagi menjayakan penyelidikan ini.RUJUKANAGBOSSOU, A, P. MELE and N. ALBEROLA. 1994. Strain Rate and Coupling Agent Effect inDiscontinuous Glass Fiber Reinforced Polypropylene Matrix. Journal oj CompositeMaterials 28(9): 821-836.BIG, D.M. 1987. Mechanical properties of particulate filled polymers. Polymer Composites,8: 115-122.BRISCOE, B. j. and R. W. NOSKER. 1985. The flow stress of high density polyethylene athigh rates of strain. Polymer Communications 26: 307-308.BRYAN HARIus. 1986. Engineering Composite Material yd. 1. London: The Institute of Metals.COWLEY, K. D. and P. W. R. BEAUMONT. 1997. The interlaminar and intralaminar fracturetoughness of carbon fibre/ polymer composites: The effect of temperature. CompositeScience and Technology 57: 1433-1444.DETASSIS, M., A PEGORETTI and C. MIGLIARESI. 1995. Effect of Temperature and Strain Rateon Interfacial Shear Stress Transfer I Carbon / Epoxy Model Composites. CompositesScience and Technology 53: 39-46.DONNET,j. B. and P. EHRBURGER. 1977. Carbon fibre in polymer reinforcement. Carbon 15:143-152.FIGUEIREDO, j. L., C. A BERNARDO, R. T. K. BAKER and K. j. HOTTINGER. 1990. Carbon FibresFilaments and Composites. London: Kluwer Academic Publishers.PertanikaJ. Sci. & Techno!. Vol. 8 No.2, 2000 123Sahrim Hj. Ahmad dan Nor Hasimah MohamedHARTl GSVELDT, E. A. A. V. andJ.J. V. AARTSEN. 1991. Strain-rate dependence of interfacialadhesion in particle-reinforced polymers. Polymer 32(8) : 1482-1487.KARAN, G. N. 1991. Effect of fibre volume on tensile properties of real unidirectionalfibre-reinforced composites. Composites 22 (2): 84-88.KREKEL, G., K. J. HOrrINGER and W. P. HOFFMAN. 1994. The relevance of the surfacestructure and surface chemistry of carbon fibers in their adhesion to high temperaturethermoplastics: Part II Surface chemistry. Journal oj Materials Science 29: 3461-3468.MADER, E. 1997. Study of fibre surface treatments for control of interphase properties incomposites. Composites Science and Technology 57: 1077·1088.MOHO ISHAK, Z. A. and J. P. BERRY. 1993. Impact properties of short carbon fiberreinforced nylon 6.6. Polymer Engineering and Science 33: 1483-1487.NAKAo, F., Y. TANAKA and H. AsAl. 1992. Surface characterization of carbon fibres andinterfacial properties of carbon fibre composites. Composites 23: 365-372.NICOLAlS, L. and M. NARKJs. 1971. Stress-strain behavior of styrene-acrylonitrile/glass beadcomposites in the glassy region. Polymer Engineering and Science 11(3): 194-199.SAWADA, Y., Y. NAKANISHI and T. FUKUDA. 1993. Effect of carbon fibre surface on interfacialadhesive strength in CFRP. Composites 24: 573-579.THOMASON, J. L. and M. A. VLUG. 1996. Influence of fibre length and concentration onthe properties of glass fibre-reinforced polyethylene: 1. Tensile and flexural modulus.Composites 27A: 477-484.Wu, H. F. 1991. Effect of temperature and strain rate on tensile mechanical propertiesof ARALl.rllaminates. Journal oj Material Science 26:3721-3729.ZIELKE, D., K. J. HOTTINGER and W. P. HOFFMAN. 1996. Surface-oxidized carbon fibers: II.chemical modification. Carbon 34: 999-1005.124 PertanikaJ. Sci. & Techno\. Vo\. 8 No.2, 2000

Kesan Suhu dan Kadar Terikan ke atas Sifat Regangan

Komposit Getah Asli Tennoplastik (HDPE/NR)

Berpenguat Gentian Karbon Pendek

http://psasir.upm.edu.my/3537/1/Kesan_SOOu_dan_Kadar_Terikan_ke_atas_Sifat_Regangan.pdf

Kesan Suhu dan Kadar Terikan ke atas Sifat Regangan Komposit Getah Asli Tennoplastik (HDPE/NR) Berpenguat Gentian Karbon Pendek

Abstract

Similar works

Full text

Available Versions

Universiti Putra Malaysia Institutional Repository