The construction of a system for simultaneous multiple sample resistance measurement of high-temperature superconductors is reported. The data acquisition system uses the PCLD785B relay board controlled by parallel

input-output 8255A PIA emulation through a PCL724B card to perform multisample measurements by signal switching. The system, which is controlled by a 80486 microcomputer, is able to log, store and plot temperature and resistance readings and can be modified to accommodate up to six samples per run. The temperature can be measured with a precision of 0.1 K and accuracy of ±1 K. The absolute-zero offset value is less than 0.1 K. The maximum switching voltage, maximum current and open channel isolation

resistance are 125 V, 2 A and 100 MQ, respectively. The closed channe

Md Salleh, Faizah

Yahya, Ahmad Kamal

Universiti Putra Malaysia Institutional Repository

Pertanika J. Sci. & Techno!. 7(1): 25 - 32 (1999)ISSN: 0128-7680© Universiti Putra Malaysia PressMultisample Data Acquisition System for ResistanceMeasurement of High-temperature SuperconductorsAhmad Kamal Yahya, Faizah Md. Salleh and R. Abd-Shukor1School of Applied SciencesInstitut Teknologi Mara40450 Shah Alam, Selangor, MalaysiaI School of Applied PhysicsUniversiti Kebangsaan Malaysia43600 Bangi, Selangor, MalaysiaReceived 17 September 1996ABSTRAKPembinaan satu sistem pengukuran rintangan superkonduktor suhu tinggiberbilang sam pel secara serentak dilaporkan. Sistem perolehan data inimenggunakan kad geganti PCLD785B yang dikawal menggunakan input-<>utputselari emulasi 8255A PIA melalui kad PCL724B untuk melaksanakan ujianberbilang sampel dalam masa serentak melalui kalihan isyarat. Sistem yangdikawal oleh mikrokomputer 80486 ini berupaya mencatat, menyimpan danmemplot graf bagi bacaan-bacaan suhu melawan rintangan dan dapat diubahsuaiuntuk menguji sehingga enam sampel secara serentak. Suhu boleh diukurdengan kepersisan 0.1 K dan ketepatan ±1 K. Nilai imbangan sifar-mutlakadalah kurang daripada 0.1 K. ilai voltan maksimum, arus maksimum danrintangan pengasingan salur terbuka adalah masing-masing 125 V, 2 A dan 100MQ. Nilai rintangan saluran tertutup adalah kurang dari lQ setiap saluran danofset terma saluran kurang dari 5 ~V. Tempoh diam minima 1 digunakankerana mengambil kira masa operasi geganti dan tempoh lepasnya dan jugauntuk membolehkan bacaan jangkasuhu dan pengawal untuk menetap padasetiap perubahan saluran. Pengukuran rintangan meJawan suhu bagisuperkonduktor RB~Cu307'¢ (R=Y dan Er) dan variasinya telah dijalankan dandibandingkan dengan keputusan yang terdahulu.ABSTRACTThe construction of a system for simultaneous multiple sample resistancemeasurement of high-temperature superconductors is reported. The dataacquisition system uses the PCLD785B relay board controlled by parallelinput-output 8255A PIA emulation through a PCL724B card to performmultisample measurements by signal switching. The system, which is controlledby a 80486 microcomputer, is able to log, store and plot temperature andresistance readings and can be modified to accommodate up to six samplesper run. The temperature can be measured with a precision of 0.1 K andaccuracy of ±1 K. The absolute-zero offset value is less than 0.1 K. Themaximum switching voltage, maximum current and open channel isolationresistance are 125 V, 2 A and 100 MQ, respectively. The closed channelAhmad Kamal Yahya, Faizah Md. Salleh and R. Abd-ShukorResistance measurement was done using the 4-point-probe technique. ALakeShore dc current source (Model 120 CS) was employed. The voltage across thesample was measured by Keithley Model 197 (5 Xdigit) digital multimeter (DMM)connected through the IEEE-488 interface to the computer. A second DMM wasused to measure the resistance across the platinum resistor temperature sensor.The current on/off switching and multisample switching were achievedusing the PCLD785B 24-channel relay output board connected to a PCL724B,which is a 24-bit digital I/O card using a 50-pin OPTO-22 connector. Eachchannel of the PCL724B card has single pole, double throw (SPDT) relayswitches each with a normally closed ( C) and normally open ( 0) terminal.The relay operates for a TTL low on the input and releases for a TTL high. Themaximum switching voltage, maximum switching current and open channelisolation resistance are 125 V, 2 A and 100 MQ, respectively. The closedchannel resistance is less than 1 Q per pole and channel thermal offset is lessthan 5 /lV. A minimum scan dwell time of 1 s was used to accommodate therelay operation time of 8 ms and a similar release time to allow the thermometerand controller to settle on channel changes.In our configuration we used only the NC terminals of the relays forelectrical contact to prevent any open circuit voltage and magnetic mechanismof the relay from contributing noise to the system. The samples were connectedto the DMM and current source through the relays (Fig. 1). In this configuration,a total of four C output of the relays were used for each sample. The systemcan be easily programmed for a specific scan sequence and can also accommodateup to six samples per run. Fig. 2 shows the 4-wire switching configuration whichallows current to be sourced to two closely spaced samples, one at a time andPCLD 7858 CardICurrent +1 I .- +1Source -I~ CI I+YI DMM ~+ C2 .---;~(Yoll) of-' rl,.----t \.....-I /.- f-;y-C3~C4 .--I.-f .::!..C5...... +Yr- C6t--'......-:v-~ C7 .-C8 1.--/~To ChannelsC910C24To Sample ITo Sample 2low) ofncewethe186.ersfortheun~ntLrelesLer)rtaIAbytaut.alre-dIetolyd1,o28Fig 2. Schematic of the 4-wire switching configuration on the PC1D785B cardPertanikaJ. Sci. & Techno!. Vo!. 7 No.1, 1999Multisample Data Acquisition System for Resistance Measurement of Superconductorssimultaneously reading the voltage drop across each sample. The sample holderwas made from oxygen-free high conductivity copper (OFHC) material fromLakeShore Cryotronics, SA, which has a very high thermal conductivity (500-550 W/m·I.KI) to ensure uniformity of temperature between samples.Experimental ProcedureTwo samples were mounted on a copper sample holder attached to the coldhead of the cryostat. The distance between the current leads was about 10 mmand the distance between the voltage leads about 5 mm. Silver conductive paintwas used for electrical contact and a 30 rnA direct current was used. A typicalvalue of voltage across the sample at room temperature was 200 J.l.V.Resistance was measured between 78 - 300 K. During a particular acquisitioncycle, the sample temperature T was increased at a specified rate (for example 5Klmin). The system can be programmed to log in data for a specified temperatureinterval (for example, 3 K) or changes in voltage (for example, 2 J.l.V) across thesample. Since the relay operation and release time were around 8 ms, theappropriate delay time was introduced before each measurement was made. Thecomputer then switched the electrical connections to the next sample where thecorresponding (T, V) values were measured. During the measurement, a voltage-temperature curve was plotted on the computer screen along with a numericaldisplay of the data (T, V). The software flow diagram is shown in Fig. 3.RESULTS AND DISCUSSIONThe powder X-ray diffraction (not shown) of the YBa2Cu307_~ andY(Ba09CaO.l)2Cu307-li indicates a single phase, orthorhombic "123" phasebelonging to the space group P4/mmm . The ErBa2Cu307-li and ErBa2Cu30 7-li-Ag composite also showed a dominant "123" phase.Fig. 4 shows the normalized resistance versus temperature curve for YB~Cu307_~ and Y(Bao.gCaO.I)2Cu307-li samples. Both curves showed metal-like normal statebehaviour. The measurements on YB~Cu307-Oare comparable to earlier reports(see, for example, Kirkup 1988) with onset temperature (Tconse) 92 K and zero-resistance temperature (Tc zero) 89 K. The Tc onset of Y(Bao.9CaO.l)2Cu307-li was 89 Kand Tczero 80 K. Work on the effect of Ca doping on the Ba site in Y(Ba l .xCa)2Cu307-li is in progress and will be reported elsewhere.The curves for both the pure ErB~Cu307-liand ErB~Cu307-li-Ag compositealso showed metal-like normal state behaviour (Fig. 5). The ErB~Cu307-lisamplehad T of 91 K and T of 88 K. The measurements on ErR" Cu30 7< werec onset c zero ~ -Qcomparable to earlier reports (Maletta et at. 1989; Bichile et at. 1990). The ErBa2Cup7_~ Ag composite showed significantly higher Tc onset (95 K) and Tc zero (90 K). Theoxygen content (calculated using results from Bichile et at. 1990) of the pureErBa2Cu30 7-li sample was approximately 6.9. The increase in Tc of the ErB~Cu307_~ - Ag composite may have been due to a slight increase in the oxygen content(slightly above 6.9) due to the addition of Ag. This seems to be consistent withincrease in oxygen intake as a result of Ag addition in YBa2Cu30 7-li (Moya et al.PertanikaJ. Sci. & Techno!. Vo!. 7 o. 1, 1999 2930Ahmad Kamal Yahya, Faizah Md. Salleh and R. Abd-ShukorStartInitialize VariableRun= I, Sample = 0Tree = 0, Vree = 0Sample=ORead T, VNO>-----.1 RUN = RUN + 1Fig 3. Logic flow diagram oj the data acquisition systemPertanikaJ. Sci. & Technol. Vol. 7 No.1, 1999Multisample Data Acquisition System for Resistance Measurement of Superconductors10.820 0.60c<l~~ 0.4~0.2060 120 180 240 30Temperature (K)Fig 4. ormalized resistance versus temperature ojYBa2Cu]07.(, and Y(BaO.9CaO)2Cu]Oj.(,260160 210Temperature (K)110",.'*'-"",,.,.....'ErBaCuO ,.",-~ ,.,....r-_/. _.,r" ErBaCuO + Ag; ---~._.ifii.',.';:J!o +---....;...-'"""T------.------,-----I-600.75200 0.5c<l~E0::0.25Fig 5. onnalized resistance versus temperature ojErBa2Cu]07.(, and ErBa2Cu]07.(, - Ag composite1990). Further investigations on the effect of Ag in ErBa2Cu3c(,..-; are in progressand will be reported elsewhere.The data acquisition system was able to detect minute variations in theresistance profile and transition temperature (± 1 K) of high temperaturesuperconductors. These results indicate that the low-eost relays on the PCLD785B24-channel relay output board did not introduce any noise detrimental to thelow temperature measurement when used in the above configuration. Since aPertanikaJ. Sci. & Techno!. Vo!. 7 o. I, 1999 31Ahmad Kamal Yahya, Faizah Md. Salleh and R. Abd-Shukortotal of four channels are needed for each sample, the system can be expandedto accommodate a maximum of six samples per run.The system can be further improved by using a programmable currentsource with built-in IEEE-488 interface which will allow the system to automaticallyreverse current direction or vary current magnitude during a thermal scan,which could prevent possible heating of samples by the current leads. Thesensitivity of the system may also be upgraded by using a nanovoltmeter in placeof the 5 Y; digit DMM for voltage readings.ACKNOWLEDGEMENTSResearch at ITM and UKM was supported by Bureau of Research and Consultancy(BRC) and Malaysia Toray Science Foundation, respectively.REFERENCESAHMAD KAMAL YAHYA, R. Ano-SHUKOR and FAIZAH MD. SALLEH. 1996. Data acquisition systemfor resistance measurement of high-temperature superconductors. PCltanika J. Sc.Technol. 4: 231-237.BICHILE, G.K., D.G. KUBERKAR and S.S. SHAH. 1990. Influence of the oxygen stoichiometryon the structure and superconducting properties of Er-Ba-Cu-O system. Solid SlaleComm. 74: 629-632.KIRKUP, L. 1988. Resistance measurements as a function of temperature on the high-tcsuperconductor YBa2Cu30 7.• Eur. J. Physics 9: 4.MALETTA, H., E. P"RSCHKE, B. Rupp and P. MEUFFELS. 1989. On the suppression ofsuperconductivity in ErBa2Cupx' Z. Phys. B 77: 181-184.MoYA, J.S. and E. SAIZ. 1990. Preparation of YBaCuO-Ag composites by control of thesintering atmosphere. Solid Slale Comm. 74: 1291-1294.OUSEPH, PJ., D. BRUNING, M.R. O'Brian, J.P. ° SEPI-I and S. CARTER. 1989. Automaticmeasurement of resistance of high-temperature superconductors. Rev. Sci. Inslrum,60(3): 511-512.32 PertanikaJ. Sci. & Techno!. Vo!. 7 No.1, 1999

Multisample Data Acquisition System for Resistance

Measurement of High-temperature Superconductors

http://psasir.upm.edu.my/3478/1/Multisample_Data_Acquisition_System_for_Resistance.pdf

Multisample Data Acquisition System for Resistance Measurement of High-temperature Superconductors

Abstract

Similar works

Full text

Available Versions

Universiti Putra Malaysia Institutional Repository