Research study on materials processing in space, M566 experiment

Abstract

Specimens of the aluminum-33 wt% copper eutectic partially melted and resolidified in the low effective gravity of the orbiting Skylab were examined and characterized with respect to microstructural defects and thermal conductivity values. The results obtained were compared with similar evaluations of ground-based simulation melt-resolidification experiments and as-prepared unidirectionally solidified specimens. Thermal conductivity data and electrical resistivity data at temperatures from 25 C to 400 C did not show significant differences between ground and space processed specimens. A methology of evaluating the defects in the Al-Al2Cu structure was implemented. A specimen from Skylab 3 showed signs of instability in growth and several grains were found in the ingot. The specimen from Skylab 4 did not show such marked instability in growth and was found to contain fewer defects than the ground-processed specimens. This agrees with data from Georgia Institute of Technology which showed that there were fewer defects in both their Skylab 3 and 4 specimens than in ground processed specimens