Endurance and failure characteristics of main-shaft jet engine bearings at 3x10 to the 6th power DN

Abstract

Groups of thirty 120-mm bore angular contact ball bearings were endurance tested at a speed of 12,000 and 25,000 rpm and a thrust load of 66 721 N. The bearings were manufactured from a single heat of VIM-VAR AISI M-50 steel. At 1.44X1 million and 3.0x1 million DN, 84 483 and 74 800 bearing test hours were accumulated, respectively. Test results were compared with similar bearings made from CVM AISI M-50 steel run under the same conditions. Bearing lives at speeds of 3x1 million DN with the VIM-VAR AISI M-50 steel were nearly equivalent to those obtained at lower speeds. A combined processing and material life factor of 44 was found for VIM-VAR AISI M-50 steel. Continuous running after a spall has occurred at 3.0x1 million DN can result in a destructive fracture of the bearing inner race