Testing of polyimide second-stage rod seals for single-state applications in advanced aircraft hydraulic systems

Abstract

Machined polyimide second-stage rod seals were evaluated to determine their suitability for single-stage applications where full system pressure acts on the upstream side of the seal. The 6.35-cm (2.5-in.) K-section seal was tested in impulse screening tests where peak pressure was increased in 3.448-MPa (500-psi) increments each 20,000 cycles. Seal failure occurred at 37.92 MPa (5,500 psi), indicating a potential for acceptability in a 27.58-MPa (4,000-psi) system. Static pressurization for 600 sec at pressures in excess of 10.34 MPa (1,500 psi) revealed structural inadequacy of the seal cross section to resist fracture and extrusion. Endurance testing showed the seals capable of at least 65,000 1.27-cm (0.5-in.) cycles at 450 K (350 F) without leakage. It was concluded that the second-stage seals were proven to be exceptional in the 1.379-MPa (200-psi) applications for which they were designed, but polyimide material properties are not adequate for use in this design at pressure loading equivalent to that present in single-stage applications