The effects of composites as adherends was studied. Several other variables were studied by fractography: aluminum powder adhesive filler, fiber glass cloth scrim or adhesive carrier, new adhesives PPQ-413 and LARC-13, and strength-test temperature. When the new results were juxtaposed with previous work, it appeared that complex interactions between adhesive, adherend, bonding, and testing conditions govern the observed strength and fracture-surface features. The design parameters likely to have a significant effect upon strength-test results are listed

Dwight, D. W.

Wightman, J. P.

English

NASA Technical Reports Server

A fundamental approach to adhesion:  Synthesis, surface analysis, thermodynamics and mechanics

The ability of SEM/EDAX to determine the physical and chemical composition of very small areas was used to study several diverse types of samples representative of NASA-LaRC technology. More systematic investigation was carried out on differences in the results of grit-blasting Ti 6-4 adherends and the presence of extraneous elements, primarily silicon, in some polymer/HT-S fiber composites. Initial results were obtained from a fractured (ILS) short-beam shear specimen, and from Ti 6-4 alloy, before and after a proprietary Boeing anodizing surface preparation for adhesive bonding. Photomicrographs and EDAX spectra were also obtained from new, fractured lap shear strength specimens that employed PPQ and LARC-13 adhesives

A fundamental approach to adhesion: Synthesis, surface analysis, thermodynamics and mechanics

Abstract