X-ray photoelectron spectroscopic study of surface chemistry of dibenzyl-disulfide on steel under mild and severe wear conditions

Abstract

Wear tests were performed on 304 stainless steel lubricated with pure mineral oil with and without dibenzyl-disulfide. Both mild and severe wear were observed. The type of wear was distinguished by a marked change in wear rate, friction coefficient, and wear scar appearance. The chemical composition of the wear scar surface was examined with X-ray photoelectron spectroscopy in conjunction with argon ion sputter etching. In severe wear scars, a sulfide was formed at the expense of the normal oxide layer. In mild wear scars, there were only superficial sulfur compounds, but there was a substantial increase in the oxide thickness