Carburization and heat treatment to cause carbide precipitation in gamma/gamma prime-delta eutectic alloys
- Publication date
- Publisher
Abstract
In an attempt to improve their longitudinal shear strength, several directionally solidified eutectic alloy compositions with minor element modifications were pact, carburized, and heat treated to provide selective carbide precipitation at the cell and grain boundaries. The directionally solidified Ni-17.8 Nb-6Cr-2.5Al-3Ta (weight percent) alloy was selected for the shear strength evaluation because it showed the shallowest delta-denuded zone at the carburized surface. The carburization-carbide precipitation treatment, however, did not appear to improve the longitudinal shear strength of the alloy