Evaluation of SSME high pressure liquid oxygen turbopump bearings

Abstract

Examination of the bearings produced conclusive evidence that a very high axial load was applied to bearing 8517903 during a significant portion of the service time. The high loads caused serious ball and race wear and surface fatigue pitting. In all likelihood, continued operation of this bearing with the high axial load would have caused increasing deterioration and catastrophic failure. In contrast, bearing 8517900 showed much less deterioration and probably had experienced only the axial loads deliberately applied by the preload spring. Bearing 8517900 represents the best-case operation with the loads controlled to the levels intended in the design. Fatigue life calculations on bearing 8517903 with an axial load of 27,000 N showed the intolerance of the bearing to such load levels