Technological development of cylindrical and flat shaped high energy density capacitors

Abstract

Cylindrical wound metallized film capacitors rated 2 micron F 500 VDC that had an energy density greater than 0.3 J/g, and flat flexible metallized film capacitors rated at 2 micron F 500 VDC that had an energy density greater than 0.1 J/g were developed. Polysulfone, polycarbonate, and polyvinylidene fluoride (PVF2) were investigated as dielectrics for the cylindrical units. PVF2 in 6.0 micron m thickness was employed in the final components of both types. Capacitance and dissipation factor measurements were made over the range 25 C to 100 C, and 10 Hz to 10 kHz. No pre-life-test burning was performed, and six of ten cylindrical units survived a 2500 hour AC plus DC lift test. Three of the four failures were infant mortality. All but two of the flat components survived 400 hours. Finished energy densities were 0.104 J/g at 500 V and 0.200 J/g at 700 V, the energy density being limited by the availability of thin PVF2 films