Pressureless sintered beta prime-Si3N4 solid solution: Fabrication, microstructure, and strength

Abstract

Si3N4, AlN, and Al2O3 were used as basic constituents in a study of the pressureless sintering of beta prime-Si3N4 solid solution as a function of temperature. Y2O3-SiO2 additions were used to promote liquid-phase sintering. The sintered specimens were characterized with respect to density, microstructure, strength, oxidation, and thermal shock resistance. Density greater than 98 percent of theoretical was achieved by pressureless sintering at 1750 C. The microstructure consisted essentially of fine-grained beta prime-Si3N4 solid solution as the major phase. Modulus of rupture strengths up to 483 MPa were achieved at moderate temperature (1000 C), but decreased to 228 MPa at 1380 C. This substantial strength loss was attributed to a glassy grain boundary phase formed during cooling from the sintering temperature. The best oxidation resistance was exhibited by a composition containing 3 mol % Y2O3-SiO2 additives. Water quench thermal shock resistance was equivalent to that of reaction sintered silicon nitride but lower than hot-pressed silicon nitride