High Velocity Burner Rig Oxidation and Thermal Fatigue Behavior of Si3N4- and SiC Base Ceramics to 1370 Deg C

Abstract

One SiC material and three Si3N4 materials including hot-pressed Si3N4 as a baseline were exposed in a Mach-1-gas-velocity burner rig simulating a turbine engine environment. Criteria for the materials selection were: potential for gas-turbine usage, near-net-shape fabricability and commercial/domestic availability. Cyclic exposures of test vanes up to 250 cycles (50 hr at temperature) were at leading-edge temperatures to 1370 C. Materials and batches were compared as to weight change, surface change, fluorescent penetrant inspection, and thermal fatigue behavior. Hot-pressed Si3N4 survived the test to 1370 C with slight weight losses. Two types of reaction-sintered Si3N4 displayed high weight gains and considerable weight-change variability, with one material exhibiting superior thermal fatigue behavior. A siliconized SiC showed slight weight gains, but considerable batch variability in thermal fatigue