Solidification (crystal growth) in the presence of gravitational forces

Abstract

The surface tension behavior of doped and undoped InSb melts was investigated as well as their temperature and composition dependence. Surface tension in InSb melts was determined using the sessile-drop technique covering the temperature range from 530 C to 880 C. A linear regression of the data obtained shows that the temperature dependence of sigma is 392- (T-530) x (7000) plus or minus 10 dyne/cm. The d sigma/d Tau for intrinsics InSb is less than that previously reported. On the basis of the surface tension data obtained, it is concluded that surface tension induced convective flow velocities in InSb under reduced gravity conditions range from zero to at most 1 cm/sec. Accordingly, no interference with dopant segregation can be expected during growth in space because the momentum boundary layer (at the crystal melt interface) associated with any Marangoni-type convective flows would, at the given growth rate, be significantly larger than the predicted diffusion boundary layer thickness