Ultrasonic attenuation as an indicator of fatigue life of graphite/epoxy fiber composite

Abstract

The narrow band ultrasonic longitudinal wave velocity and attenuation were measured as a function of the transfiber compression-compression fatigue of unidirectional graphite/epoxy composites. No change in velocity was detected at any point in fatigue life. For specimens fatigued at 80% of static strength, there was generally a 5% to 10% increase in attenuation, however, this increase does not appear to be a satisfactory indicator of fatigue life. On the other hand, there appears to be a correlation between initial attenuation (measured prior to cycling) and cycles to fracture. Initial attenuation as measured at 1.5 MHz and 2.0 MHz appears to be a good indicator of relative fatigue life