An Experimental Evaluation of Oil Pumping Rings

Abstract

The design and construction of a reciprocating test vehicle to be used in evaluating hydrodynamic oil pumping rings are discussed. In addition, experimental test data are presented for three pumping ring designs that were constructed from Tin-Based Babbitt (SAE 11), Bearing Bronze (SAE 660), and Mechanical Carbon Graphite (Union Carbide Grade CNF-J). Data of pumped flow rate versus delivered pressure, as well as friction loss, are reported for the following conditions: frequencies of 10, 35 and 45 Hz; strokes of 25.4 mm (1.00 in.), 38.1 mm (1.50 in.) and 50.8 mm (2.00 in.) oil inlet temperature of 49 degrees (120 degrees); and pumping ring close-in pressures of 10.3 MPa (1500 lb/square inch. A 20W40 automotive oil was used for all tests. The maximum delivered pressure was 11 MPa (1600 lb/square inch. An analysis of hydrodynamic oil pumping rings was performed and the results of the analysis were compared to measured test data