Prediction of fatigue crack-growth patterns and lives in three-dimensional cracked bodies

Abstract

Fatigue crack growth patterns and lives for surface cracks, surface cracks at holes, and corner cracks at holes in three dimensional bodies were predicted using linear-elastic fracture mechanics concepts that were modified to account for crack-closure behavior. The predictions were made by using stress intensity factor equations for these crack configurations and the fatigue crack-growth (delta K against rate) relationship for the material of interest. The crack configurations were subjected to constant-amplitude fatigue loading under either remote tension or bending loads. The predicted crack growth patterns and crack growth lives for aluminum alloys agreed well with test data from the literature