Evaluation of Ti-6Al-4V surface treatments for use with a polyphenylquinoxaline adhesive

Abstract

Three surface treatments for Ti-6Al-4V adherends were evaluated using a thermoplastic polymer monoether polyphenylquinoxaline, MEPPQ, which had been shown in previous studies to have good potential as a high temperature adhesive for aerospace applications. Initial results based on long term thermal exposure at 232 C (450 F) using the phosphate-fluoride (PF) and chromic acid anodized (CAA) treatments with MEPPQ adhesive were not encouraging. A significant improvement in strength retention and a change in failure mode (cohesive) at 232 C (450F) was found for the SHA treated specimens compared to the PF and CAA treatments. Although an improvement in long term thermal durability was obtained with the SHA treatment of Ti-6Al-4V, an improved surface treatment with better long term durability is still required for aerospace applications