The interlaminar fracture toughness of woven graphite/epoxy composites

Abstract

The interlaminar fracture toughness of 2-D graphite/epoxy woven composites was determined as a function of stacking sequence, thickness, and weave pattern. Plain, oxford, 5-harness satin, and 8-harness satin weaves of T300/934 material were evaluated by the double cantilever beam test. The fabric material had a G (sub Ic) ranging from 2 to 8 times greater than 0 degrees unidirectional T300/934 tape material. The interlaminar fracture toughness of a particular weave style was dependent on whether the stacking sequence was symmetric or asymmetric and, in some cases, on the fabric orientation