The 3F condensation polyimides: Review and update
- Publication date
- Publisher
Abstract
Nine new condensation polyimides containing the phenyltrifluoroethylidene (3F) linkage were synthesized by the amic-acid route. Several other polyimides, including some with hexafluoroisopropylidene (6F) linkage, were also prepared as controls. Amic-acid solutions were characterized by determining their inherent viscosities prior to thermal conversion into polyimide films. Glass transition temperatures (T sub g), thermogravimetric analysis (TGA), and isothermal weight loss data (at 316, 371, and 371 C under 0.5 MPa air pressure) were obtained for the films. The films were pulverized into molding powders which, in turn, were thermally processed under pressure into neat resin disks. The disks were also characterized by T sub g's and 316 and 371 C isothermal weight losses. The film study identified two new polyimides with T sub g's greater than 371 C and two new polyimides with low rates of weight loss. The resin disks exhibited the same overall trends in T sub g and weight loss as the respective films, however the weight loss per unit surface area was always greater, presumably due to molecular degradation induced during preparation of the molding powders. The overall results indicate that polyimides containing the 3F linkage have T sub g's and thermo-oxidative stability comparable to polyimides containing the 6F group. Alternate technology was also shown by the synthesis of two new polyalkyl substituted 3F diamines and five more new 3F polymers. Their potential as photoresists was demonstrated by T sub g advancement after ultraviolet exposure. Last, four U.S. patents on 3F monomers and polymers were issued and up to eight more are pending