Microcracking mechanisms and interface toughening of semi-IPN polyimide matrix composites

Abstract

A new research program was initiated as a preliminary phase. The following three objectives are being pursued for the overall program: to elucidate the mechanisms of microcracking for graphite fiber-reinforced semi-IPN polyimide matrix composites under mechanical and thermal cyclic loading; to devise material engineering solutions for possible improvement of fatigue damage resistance (or the increase of fatigue endurance strength) of semi-IPN matrix composites by tailoring of modulus and toughness of fiber-resin interface region; and to assess processing characteristics of the composites and their roles in controlling the resistance of composites to microcracking and the effectiveness of interface toughening. The main emphasis was placed upon the initial screening of material systems and optimization of processing conditions for semi-IPN matrix composites with tailored interface. As a first set of control material systems to study, the composites were prepared with unsized Celion 6000 graphite fiber reinforcement and the following resin matrices of varied fracture toughness: PMR-15 thermoset polyimide, semi-IPN of PNR-15 thermoset polyimide and NR150B2 thermoplastic polyimide in 75/25 ratio, and semi-IPN of PMR-15 and NR150B2 in 50/50 ratio. For the composites with the resin matrix of semi-IPN in 75/25 ratio, interface tailoring was attempted by using graphite fibers coated with the resins of systematically varied fracture toughness. In the continuing work, a broad range of interlayer toughness will be achieved by coating the fibers with reactants of semi-IPN having lower or higher content of thermoplastic constituent in comparison with the composition of surrounding resin matrix. In pursuing the objectives of the overall research program, the respective roles and interaction of critical parameters were defined