Evaluation of advanced lubricants for aircraft applications using gear surface fatigue tests

Abstract

Surface pitting fatigue life tests were conducted with five lubricants, using spur gears made from a single lot of consumable-electrode vacuum melted (CVM) AISI 9310 steel. The gears were case carbonized and hardened to a Rockwell c-60 and finish ground. The gear pitch diameter was 8.89 cm. The lot of gears was divided into five groups, each of which was tested with a different lubricant. The test lubricants can be classified as synthetic polyol-esters with various viscosities and additive packages. Test conditions included bulk gear temperature of 350 K, a maximum Hertz stress of 1.71 GPa (248 ksi) at the pitch line, and a speed of 10,000 RPM. The lubricant with a viscosity that provided a specific film thickness greater than one and with an additive package produced far greater gear surface fatigue lives than lubricants with a viscosity that provided specific film thickness less than one. A low viscosity lubricant with an additive package produced gear surface fatigue lives equivalent to a similar base stock lubricant with 30 percent higher viscosity, but without an additive package. Lubricants with the same viscosity and similar additive packages gave equivalent gear surface fatigue lives