Investigation of effect of fluoride on corrosion of 2S-0 aluminum and 347 stainless steel in fuming nitric acid at 170 F

Abstract

The effect of small additions of fluoride on the corrosion of 2S-0 aluminum and 347 stainless steel by fuming nitric acid at 170 degrees F has been evaluated quantitatively by the determination of the weight loss of metal specimens immersed in the acid. The ratio of metal surface area to volume of acid was approximately 7.5 inch (superscript)-1 in all cases. It was found that for acids containing no fluorides the weight loss of aluminum was approximately 1/5 that of stainless steel. Addition of 1 percent fluoride ion to the acid reduced the weight loss of both metals to practically zero even after 26 days of exposure to the acid at 170 degrees F. The minimum quantity of fluoride ion required to inhibit corrosion was found to be approximately 0.25 and 0.5 percent for aluminum and stainless steel, respectively, in white fuming nitric acid and 0.5 and 1 percent in red fuming nitric acid (18 percent nitrogen dioxide). These fluoride percentages were based on the total weight of acid. Provided the concentration of fluoride ion was sufficient to inhibit corrosion, the source of these ions was immaterial. Additional information concerning the effect of fluorides on corrosion was obtained by measuring the electrode potentials of the metals against a platinum reference electrode

    Similar works