Investigation of static and cyclic bearing failure mechanisms for GR/EP laminates
- Publication date
- Publisher
Abstract
Static, cyclic load (fatigue), and residual strength testing of graphite-epoxy (GR/EP) and aluminum pin bearing joints was completed to study bearing failure mechanisms. Parameters investigated included static strength, failure mode, fatigue life, hole growth, joint stiffness, and residual strength. Comparative evaluation of these results show that the MIL-HDBK-5 convention for the definition of bearing strength can be used for GR/EP materials while maintaining the same, or improved, level of structural integrity shown for metal joints