Survivability of Affordable High Temperature Polymer Matrix Composites for Propulsion Engine Components
- Publication date
- Publisher
Abstract
PMR-type polyimides are regarded as state of the art high temperature polymers, due to their excellent thermo-mechanical properties and thermo-oxidative stability. One of their drawbacks, however is the inability to process them using cost-effective processing methods such as Resin Transfer Molding (RTM) and Resin Film Infusion (RFI). Development of low viscosity, high temperature polymers has been the subject of intense research. Recently, a new generation of low viscosity polyimides were synthesized by the introduction of twisted biphenyl or binapthyl groups into the backbone. This report details the progress for Year 1, which has involved acquiring samples and initiating Phases I and II of the proposed research. Specifically, studies of the process-property relationships of a series of polymers using oligomers based on 2,3,3' ,4'-biphenyltertracarboxylic dianhydride (PBDA) and a mixture of a diamine, BAX and a triamine, 1,3,5-Tris (4-aminophenoxybenzene), TAB, where the amount of TAB was varied have been initiated. The sample containing 10 percent TAB possesses a slightly higher degree of crystalline order versus that of the 20 percent TAB sample, based on x-ray diffraction studies of the b-staged oligomers. Both systems lose all of the crystalline order upon curing, however. The chemorheology has been studied as a function of the TAB content. While the magnitude of the viscosity is essentially the same for both systems, the cure kinetics of the 10 percent TAB system is faster than that for the 20 percent TAB system. The sample exhibits a melting-recrystallization-remelting behavior before the crosslinking commences. Correlation of other kinetic parameters, such as the activation energies for curing, the Tg and mechanical properties to the structure of these systems is underway. Future studies will involve characterization of mechanical and thermal properties of the pure resins and the fabrication of fiber reinforced composites using these materials