Low Thermal Conductivity Thermal Barrier Coatings Developed

Abstract

Thermal barrier coatings (TBCs) are used extensively in modern gas turbine engines to thermally insulate air-cooled metallic components from the hot gases in the engine. These coatings typically consist of a zirconia-yttria ceramic that has been applied by either plasma spraying or physical vapor deposition. Future engines will rely even more heavily on TBCs and will require materials that have even higher temperature capability with improved insulation (i.e., lower thermal conductivity even after many hours at high temperature). This report discusses new TBCs that have been developed with these future requirements in mind. The Ultra-Efficient Engine Technology Program at the NASA Glenn Research Center is funding this effort, which has been conducted primarily at Glenn with contractor support (GE and Howmet) for physical vapor deposition. As stated, the new TBC not only had to be more insulating but the insulation had to persist even after many hours of exposure-that is, the new TBC had to have both lower conductivity and improved sintering resistance. A new type of test rig was developed for this task. This new test approach used a laser to deliver a known high heat flux in an essentially uniform pattern to the surface of the coating, thereby establishing a realistic thermal gradient across its thickness. This gradient was determined from surface and backside pyrometry; and since the heat flux and coating thickness are known, this permitted continuous monitoring of thermal conductivity. Thus, this laser rig allowed very efficient screening of candidate low-conductivity, sinter-resistant TBCs. The coating-design approach selected for these new low-conductivity TBCs was to identify oxide dopants that had the potential to promote the formation of relatively large and stable groupings of defects known as defect clusters. This approach was used because it was felt that such clusters would reduce conductivity while enhancing stability. The approach proved to be successful: low-conductivity TBCs having improved sintering resistance were developed