CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
unknown
凝胶纺壳聚糖分散碳纳米管/聚丙烯腈纤维的研究
Authors
周花
曾志群
+3 more
曾海涛
沈新元
董炎明
Publication date
15 July 2009
Publisher
Abstract
多壁碳纳米管(MWNTs)通过壳聚糖衍生物处理后与超高分子量聚丙烯腈进行复合,将得到的复合材料通过凝胶纺丝法制备出不同复合比例的MWNTs/聚丙烯腈纤维.将不同纺丝方法以及不同比例MWNTs对拉伸强度、模量、取向度、结晶结构的影响进行比较研究,同时通过电镜观察MWNTs的分散状况.结果表明:相比于湿法纺丝,通过凝胶纺丝法制备的复合纤维,MWNTs取向更好,分散更为均匀,纤维拉伸强度、模量都得到显著提高.对比未加MWNTs的对照样,在这个体系中加入质量分数为0.5%的MWNTs复合时,拉伸强度提高37%,弹性模量提高11.68%,并且声速取向度维持在相当高的水平(92.5%)
Similar works
Full text
Open in the Core reader
Download PDF
Available Versions
Xiamen University Institutional Repository
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:dspace.xmu.edu.cn:2288/158...
Last time updated on 16/06/2016