Komponentensicherheit. Abschlussbericht A Werkstoffe und Schweissverbindungen

Abstract

Within the project on reactor component safety, melts have been investigated produced from the RPV materials 22 NiMoCr 3 7 and 20 MnMoNi 5 5 in an optimized quality, a specified quality, and a quality exceeding limits. For the production-scale welding work, process parameters have been selected in compliance with the state of the art. The welds produced are free of cracks and low in coarse grain content. For transboundary welds, process parameter mofidifcations such as pin-pointed modification of heat input, bevel angle, welding sequence, and hydrogen content achieved production of welds with a coarse-grained HAZ, with macrocracks and microcracks in the HAZ and the weld, and these have been used for non-destructive and mechanical-technological experiments. (orig./UU)Untersucht wurden Schmelzen aus den Reaktordruckbehaelter-Werkstoffen 22 NiMoCr 3 7 und 20 MnMoNi 5 5 in optimierter, spezifikationsgemaesser und in grenzueberschreitender Qualitaet. Fuer die produktionsgemaessen Schweissverbindungen wurden Fertigungsparameter entsprechend dem heutigen Stand der Technik gewaehlt. Es konnten so rissfreie und grobkornarme Verbindungen hergestellt werden. Bei den grenzueberschreitenden Naehten konnten durch gezielte Aenderungen der Waermeeinbringung, des Flankenwinkels, der Schweissfolge und des Wasserstoffgehaltes Schweissnaehte mit grobkoerniger Waermeeinflusszone (WEZ) sowie mit Mikro- und Makrorissen in der WEZ und im Schweissgut fuer zerstoerungsfreie und mechanisch-technologische Versuche erzeugt werden. (orig./UU)Available from TIB Hannover: F94B1301 / FIZ - Fachinformationszzentrum Karlsruhe / TIB - Technische InformationsbibliothekSIGLEBundesministerium fuer Forschung und Technologie (BMFT), Bonn (Germany)DEGerman