Vysoká škola báňská - Technická univerzita Ostrava
Abstract
Two samples of hardwood, beech and a mixture of beech and oak were pyrolyzed by continuous chemical activation with K2CO3. Two final temperatures were tested on activated samples (550 °C, 750 °C). In the same temperature regime, also non-activated original samples were pyrolyzed. The sorption for carbonaceous material was measured with a high-pressure thermal analyzer (TGA-HP50) in the presence of nitrogen and the carbon dioxide atmosphere in the range of pressure from 0,03 to 4,5 MPa, respectively from 0,03 to 2 MPa. The sorption experiments were carried out at three different temperatures – 20, 30 a 40 °C. The tests indicate that the final temperature of activation and sorption conditions (pressure, temperature) have significant impact on sorption properties of material.Dva vzorky tvrdého dřeva, buk a směs buk/dub, byly pyrolyzovány se současnou chemickou aktivací K2CO3. Testovány byly dvě konečné teploty pyrolýzy pro aktivaci vzorků (550 °C, 750 °C). Ve stejném teplotním režimu byly pyrolyzovány i neaktivované původní vzorky. Sorpce na uhlíkové materiály byly měřeny na vysokotlakém termickém analyzátoru (TGA-HP50) v atmosféře dusíku a oxidu uhličitého v rozmezí tlaků od 0,03 do 4,5 MPa, respektive od 0,03 do 2 MPa. Sorpční experimenty probíhaly při třech teplotách – 20, 30 a 40 °C. Ukazuje se, že konečná teplota aktivace a sorpční podmínky (tlak, teplota), mají významný vliv na sorpční vlastnosti materiálu