Desorption and subsequent rehydrogenation of Mg(BH_4)_2 with and without 5 mol % TiF_3 and ScCl_3 have been investigated. Temperature programmed desorption (TPD) experiments revealed a significant increase in the rate of desorption as well as the weight percentage of hydrogen released with additives upon heating to 300 °C. Stable Mg(B_xH_y)_n intermediates were formed at 300 °C, whereas MgB_2 was the major product when heated to 600 °C. These samples were then rehydrogenated and subsequently characterized with powder X-ray diffraction (pXRD), Raman, and NMR spectroscopy. We confirmed significant conversion of MgB_2 to fully hydrogenated Mg(BH_4)_2 for the sample with and without additives. TPD and NMR studies revealed that the additives have a significant effect on the reaction pathway during both dehydrogenation and rehydrogenation reactions. This work suggests that the use of additives may provide a valid pathway for improving intrinsic hydrogen storage properties of magnesium borohydride