CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
Dynamic annealing study of SiC epilayers implanted with Ni ions at different temperatures
Authors
Gabor Battistig
J. García López
Yolanda Morilla
Publication date
22 April 2013
Publisher
'Elsevier BV'
Doi
Cite
Abstract
SiC epilayers grown on 4H-SiC single crystals were implanted with 850 keV Ni+ ions with fluences in the 0.5-9 × 1016 Ni+/cm2 range. Most of the samples were implanted at 450 °C, but for comparison some implantations were performed at room temperature (RT). In addition, a post-implantation annealing was performed in N2 at 1100 °C in order to recover the implantation-induced structural damage. The disorder produced by the implantation at 450 °C and the effect of the post-implantation annealing on the recrystallization of the substrates have been studied as a function of the fluence by Backscattering Spectrometry in channeling geometry (BS/C) with a 3.45 MeV He2+ beam. RT as-implanted samples showed a completely amorphous region which extends until the surface when irradiated with the highest dose, whereas in the case of 450 °C implantation amorphization does not occur. In general, partial recovery of the crystal lattice quality was found for the less damaged samples, and the dynamic recovery of the crystalline structure increases with the irradiation temperature. © 2009 Elsevier B.V. All rights reserved.This work is partially supported by the Projects MAT2006-03519 (Spanish MEC), P06-TEP-01739 (Junta de Andalucía) and SAB2006-0041 (Spanish MEC).Peer Reviewe
Similar works
Full text
Available Versions
Digital.CSIC
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:digital.csic.es:10261/7478...
Last time updated on 25/05/2016