CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
Interface effects on Gd induced disordering of Co films on Pt(111)
Authors
Javier Díaz
S. Ferrer
Carlos Quirós
Publication date
30 May 2012
Publisher
'Elsevier BV'
Doi
Cite
Abstract
et al.Amorphization of epitaxial Co thin films grown on top of a Pt(111) surface has been studied by surface X-ray diffraction after deposition of Gd overlayers. The results indicate strong differences of the disordering process depending on the thickness of the Co film. First basic difference is that thick Co films (15 atomic layers) are only partially amorphized by 4 atomic layers of Gd on top of them, whereas thinner Co films (5 atomic layers) are completely disordered by just 2 atomic layers of Gd. Moreover, amorphization by Gd overlayers induces different stress relaxation processes in both cases. For 15 atomic layers thick Co films a preferential amorphization of the more strained Co grains is observed, leading to an effective relaxation of about - 0.5% of the in-plane lattice parameter during amorphization, approaching its relaxed value. On the contrary, for 5 atomic layers thick Co films, the initial steps of disordering are accompanied by a stronger increase of the in-plane lattice constant, by about 1.4%, typical of Co-Pt interface alloy formation, followed by a complete amorphization. Furthermore, the magnetic characterization, carried out by magneto-optical Kerr effect and resonant magnetic surface X-ray diffraction, strongly supports that the amorphization of thin Co films is changing the nature of the Co/Pt interface. In particular, as Gd overlayers are deposited, and the amorphization proceeds, the structural disordering of the Co/Pt interface flips its characteristic perpendicular magnetic anisotropy toward in-plane orientation before the complete magnetic depolarization of the interface Pt atoms is reached. All these results confirm a marked dependence of amorphization processes on film thickness, which can be related to the enhanced influence of the nearby film/substrate interface. © 2012 Elsevier B.V. All rights reserved.Peer Reviewe
Similar works
Full text
Available Versions
Digital.CSIC
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:digital.csic.es:10261/5040...
Last time updated on 25/05/2016