Stvarni modul savijanja motki koje imaju sloj od staničnog materijala i uporaba tog modula za određivanje stvarnog modula elastičnosti staničnog materijala
Rectangular bar-shaped sandwich-like samples consisting of a cellular-material core between two standard material layers were prepared. The cellular materials were made of both ferrous and bronze hollow spheres. Using these specimens and testing method based on flexural vibrations, expected differences were observed in effective modulus values determined by means of vibrations parallel and perpendicular to layers. Information on distribution of material throughout the bar cross section was obtained through metallographic studies. The thickness of particular layers, measured values of “parallel” and “perpendicular” effective flexural modulus, and expressions derived for flexural rigidity of quasi-layered bars were used for evaluating the values of effective Young’s modulus of material of particular layers constituting the sample. Reasonable agreement was found among results obtained for various samples.Pripremljeni su pravokutni sendvič-uzorci motki koji se sastoje od jezgre sa staničnim materijalom između dva sloja standardnog materijala. Stanični materijali su napravljeni od željeznih i brončanih šupljih kugli. Uporabom tih uzoraka i metoda testiranja zasnovane na vibracijama savijanja, očekivane razlike su prijećene u postojećim vrijednostima modula određenih pomoću vibracija paralelnih i okomitih na slojeve. Informacija o rasporedu materijala u presjeku motke dobivena je na osnovu proučavanja metalografije. Debljina pojedinih slojeva izmjerenih vrijednosti “paralelnih” i “okomitih” stvarnog modula savijanja i izraza izvedenih iz savitljive krutosti poluslojevnih motki koje se koriste za procjenjivanje vrijednosti stvarnog efektnog Youngovog modula materijala pojedinih slojeva koji sačinjavaju uzorak. Razumno suglasje je pronađeno među rezultatima dobivenim za razne uzorke