The influence of strain rate on properties of microalloyed steel for cold drawing of S 315 MC and S 460 MC gra-des was analysed. It has been shown by testing these steel that strain rates in the range from 10-3 up to 1 s-1 do not influence the mechanical properties significantly. Significant strengthening started at strain rates exceeding 2 s-1. It has been shown also that the basic mechanical properties of the coldworked tested steel by 5 to 25 % were not influenced by prestrain at 10-3 to 103 s-1 strain rates. It is supposed according to the results, that the susceptibility to cold work of these steel was not influenced significantly by the strain rates usually used at coldwork (less than 1 s-1) and that the products after coldwork maintain their mechanical properties.Analiziran je utjecaj brzine naprezanja na svojstva mikrolegiranog čelika za hladno izvlačenje gradacije S 315 MC i S 460 MC. Pokazano je testiranjem tih čelika da brzine naprezanja u opsegu 10-3 do 1 s-1 ne utječu značajno na mehanička svojstva. Značajno očvršćivanje započinje kod brzina naprezanja iznad 2 s-1. Također je pokazano da osnovna mehanička svojstva hladno obrađenih čelika testiranih pri 5 do 25% ne zavise o prednaprezanju pri 10-3 do 103 s-1 brzinama naprezanja. Pretpostavljeno je na osnovi rezultata, da osjetljivost na hladnu preradu tih čelika ne zavisi značajno o brzinama naprezanja, koje se uobičajeno koriste pri hladnoj preradi (manje od 1 s-1) i da produkti zadržavaju svoja mehanička svojstva nakon hladne prerade