Deformation of the Al-Al4C3 composites with different volume fraction of Al-Al4C3 phase was investigated at different temperatures (293 - 723 K) and different strain rates (2,5 * 10-5 s-1 do 1,0 * 10-1 s-1). At temperatures 673 - 723 K and at the highest strain rate of 1,0 * 10-1 s-1, a significant ductility increase was observed. TEM analysis suggests the onset of superplasticity may be the result of dynamic grain polygonization, grain slip and rotation, partial recrystallization and dislocation creep in the tested system, which is known as strain induced dynamic recovery. Increase of the volume fraction of secondary phase in the studied composite resulted in a shift from slip on grain boundaries controlled mechanism to the grain rotation controlled deformation mechanism.Istraživana je deformacija Al-Al4C3 kompozita različitog volumnog udjela Al-Al4C3 faze kod različitih temperatura (od 293 do 723 K) i brzina deformacije (od 2,5 * 10-5 s-1 do 1,0 * 10-1 s-1). Kod temperatura od 673 do 723 K i najviše brzine deformacije od 1,0 * 10-1 s-1 zapaženo je značajno povećanje kovkosti. TEM analiza ukazuje da početak superplastičnosti može biti rezultat dinamičke poligonizacije zrna, klizanja i rotacije zrna, djelomične rekristalizacije i puzanja dislokacija u istraživanom sustavu, što je poznato kao deformacijom inducirano dinamičko oporavljanje. Porast volumnog udjela sekundarne faze u istraživanom kompozitu rezultirao je promjenom kontrolnog mehanizma deformacije od klizanja po granicama zrna do rotacije zrna