The paper presents a theoretical analysis of the asymmetrical process of rolling bimetal plates composed of the base St3S layer and a Cu cladding layer. Investigation carried out aimed at determining the curvature of bimetal band depending on the value of roll peripheral speed asymmetry factor av. Computer simulations were performed on three different layer thickness ratios, HS/HH. Numerical studies were based on computer simulations carried out using the Forge 2D software. For computations, this program uses the finite-element method. The asymmetry of the process resulted from a non-uniform distribution of rolling reduction into the bimetal band layers, which caused the band to bend at the rolling mill exit. To counteract this behaviour, an asymmetry of working roll peripheral speeds was introduced.Članak daje teorijsku analizu učinka odnosa debljine sloja bimetalnih limova sastavljenih od osnovnog sloja St3S i sloja presvučenog bakrom. Provedena istraživanja su imala za cilj odrediti zakrivljenost bimetalne trake ovisno o vrijednosti faktora asimetrije av periferne brzine. Izvedene su kompjuterske simulacije tri sloja s različitim omjerima HS/HH debljine. Numeričke studije su se zasnivale na kompjuterskim simulacijama provedenim pomoću softvera Forge 2D. Za izračune, ovaj se program služi metodom konačnih elemenata. Asimetrija procesa rezultira od nejednolikog rasporeda redukcije u slojeve bimetalne trake koje uzrokuju savijanje trake na izlazu iz valjačkog stana. Kao protuteža takvom ponašanju uvedena je asimetrija perifernih brzina radnog valjka