Due to its high void content, it has a high water percolation capacity, making it possible to reduce surface runoff. However, this compromises its mechanical resistance, which ends up restricting its use to medium traffic areas. In the present work, the properties of permeable concrete produced with different water/cement ratios (0.25; 0.30; 0.35 and 0.40) were evaluated. The characterization of the materials and the properties of the permeable concretes at 28 days were carried out. The tests carried out were resistance to axial compression, permeability, infiltration rate and Los Angeles abrasion. The final results indicated that the highest water/cement ratios used generate a higher compressive strength than the others, but with lower permeability. The resistances found reached an average of 5.15 MPa and the permeability was classified as high, when reaching values greater than 10-3 m/s.Devido ao seu alto índice de vazios, apresenta elevada capacidade de percolação de água, tornando possível a redução do escoamento superficial. No presente trabalho, foram avaliadas as propriedades de concretos permeáveis produzido com diferentes relações água/cimento (0,25; 0,30; 0,35 e 0,40). Foi realizada a caracterização dos materiais e as propriedades dos concretos permeáveis aos 28 dias. Os ensaios realizados foram de resistência à compressão axial, permeabilidade, taxa de infiltração e abrasão Los Angeles. Os resultados finais indicaram que as maiores relações água/cimento utilizadas geram uma resistência à compressão superior as demais, porém com a permeabilidade inferior. As resistências encontradas alcançaram média de 5,15 MPa e a permeabilidade foi classificada como grau alto, ao atingir valores maiores que 10-3 m/s