U-3Zr and U-20.5Pu-3Zr were injection cast into Zr tubes, or sheaths, rather than into quartz molds and clad in 316SS. These elements and standard-cast U-l0Zr and U-IgPu-l0Zr elements were irradiated in EBR-II to 2 at.% and removed for interim examination. Measurements of axial growth at indicate that the Zr-sheathed elements exhibited significantly less axial elongation than the standard-cast elements (1.3 to 1.8% versus 4.9 to 8.1%). Fuel material extruded through the ends of the Zr sheaths. allowing the low-Zr fuel to contact the cladding in some cases. Transverse metallographic sections reveal cracks in the Zr sheath through which fuel extruded and contacted cladding. The sheath is not a sufficient barrier between fuel and cladding to reduce FCCI. and any adverse effects due to increased FCCI will be evident as the elements attain higher burnup