Albany Research Center (United States. Bureau of Mines)
Abstract
Cr alloys containing 0-30 weight % W were investigated for their high temperature strength and oxidation resistance. These experimental alloys are intended for use in elevated temperature applications. Alloys were melted in a water-cooled, copper-hearth arc furnace. Microstructure of the alloys was studied using X-ray diffraction, scanning electron microscopy, and light microscopy. Meyer and Vickers hardness tests were utilized for measuring room temperature strength. A hot hardness tester with a spherical ruby indenter was used to study the strength of these materials between 800ºC and 1200ºC. A parabolic relationship was observed between load and indent size at all temperatures. On the other hand, decrease in hardness of the alloys with temperature was linear up to 1200ºC