The interaction of the components in the Gd-Mn-Sn ternary system was studied using the methods of X-ray and microstructure analyses, in the whole concentration range. The phase diagrams of the Gd-Mn-Sn system were constructed at 873 and 673 K. At both temperature of investigation the Gd-Mn-Sn system is characterized by existence of two ternary compounds: GdMn6Sn6 (MgFe6Ge6 structure type, space group P6/mmm) and Gd4Mn4Sn7 (Zr4Co4Ge7 structure type, space group I4/mmm). The formation of the interstitial solid solution GdMnхSn2 based on GdSn2 (ZrSi2-type) binary compound was found up to 10 at. % Mn at 873 K and 673 K. The existence of the substitutional solid solution based on GdMn2 (MgCu2-type) was observed up to 5 at.% Sn and 3 at. % Sn at 873 K and 673 K, respectively.Методами рентгенофазового і мікроструктурного аналізів досліджено взаємодію компонентів у потрійній системі Gd-Mn-Sn у повному концентраційному інтервалі та побудовані діаграми фазових рівноваг за температур 873 K і 673 K. За обох температур дослідження в системi утворюються дві тернарні сполуки GdMn6Sn6(структурний тип MgFe6Ge6, просторова група P6/mmm) і Gd4Mn4Sn7 (структурний тип Zr4Co4Ge7, просторова група I4/mmm). На основi бiнарного станiду GdSn2зі структурою типу ZrSi2 встановлено існування твердого розчину включення GdMnхSn2 до вмісту 10 ат. % Mn за температур 873 K і 673 K. На основі бінарної сполуки GdMn2 (структурний тип MgCu2) утворюється твердий розчин заміщення до вмісту 5 ат. % Sn при 873 K і до вмісту 3 ат. % Sn при 673 K