In this study the effect of accelerated curing on the early flexural and compressive strengths of fly ash mortars were investigated. In the mortar mixtures CEM I 42.5 R type cement and C class C fly ash with different proportions were used. 40/40/160 mm prismatic specimens were prepared from these mortars. The mortar samples cured at 7 different curing conditions. Curing conditions are standard curing, 35 ;deg;C and 85 ;deg;C hot water curing. These curing conditions applied on specimens for different times. Flexural and compressive strengths were performed on the mortar specimens. Obtained test results were comparatively evaluated. The results of this study revealed that, early age strength gain under standard curing conditions due to fly ash inclusion can be compensated by accelerated curing.Bu çalışmada; farklı miktarlarda uçucu kül içeren harçların erken yaşlardaki basınç ve eğilme dayanımlarına hızlandırılmış kür uygulamalarının etkisi incelenmiştir. Harç karışımlarında; bağlayıcı olarak CEM I 42.5 R tip çimento ve değişik oranlarda C sınıfı uçucu kül kullanılmıştır. Üretilen harçlardan 40/40/160 mm ayrıtlı prizmatik örnekler dökülerek 7 farklı kür uygulamasına tabi tutulmuştur. Kür uygulamaları standart kür, 35 °C ve 85 °C'de sıcak su kürü şeklinde ve farklı sürelerde yapılmıştır. Uygulanan kür işlemleri sonrasında harç örnekler üzerinde ortadan tekil yüklemeli eğilme ve eğilme sonrası tek eksenli basınç deneyleri gerçekleştirilmiştir. Elde edilen sonuçlar karşılaştırmalı olarak değerlendirilmiştir. Çalışma sonucunda; standart kür koşulları altında uçucu kül ikamesinin erken yaşta oluşturduğu basınç dayanım kaybının sıcak su kürü uygulaması ile telafi edilebileceği görülmüştür