Substitutional and Interstitial Diffusion in alpha2-Ti3Al(O)

Abstract

The reaction between Al2O3 and alpha2-Ti3Al was studied with a series of Al2O3/alpha2-Ti3Al multiphase diffusion couples annealed at 900, 1000 and 1100 C. The diffusion-paths were found to strongly depend on alpha2- Ti3Al(O) composition. For alloys with low oxygen concentrations the reaction involved the reduction of Al2O3, the formation of a gamma-TiAl reaction-layer and diffusion of Al and O into the alpha2-Ti3Al substrate. Measured concentration profiles across the interaction-zone showed "up-hill" diffusion of O in alpha2-Ti3Al(O) indicating a significant thermodynamic interaction between O and Al, Ti or both. Diffusion coefficients for the interstitial O in alpha2-Ti3Al(O) were determined independently from the interdiffusion of Ti and Al on the substitutional lattice. Diffusion coefficients are reported for alpha2-Ti3Al(O) as well as gamma-TiAl. Interpretation of the results were aided with the subsequent measurement of the activities of Al, Ti and O in alpha 2-Ti3Al(O) by Knudsen effusion-cell mass spectrometry