X-ray diffraction, DTA, IR and SEM investigations were carried out for a series of samples of the system NixZn1-xFe2O4 (with x=0.0, 0.2, 0.4, 0.6, 0.8 and 1.0) prepared using the usual ceramic technique. The analysis of X-ray diffraction indicates that the samples have single phase with spinel cubic structure. The lattice constant (a), radius of tetrahedral ions (rtet), bulk density (D) and theoretical density (Dx) were found to decrease while the porosity (P) increases as the content of nickel ions (x) increases. SEM images indicate observable variations between the different compositions. IR absorption spectra showed the four characteristic peaks of ferrites. The position and intensity of the peaks are markedly composition dependent.Na nizu uzoraka sistema NixZn1−xFe2O4 (za x = 0,0, 0,2 , 0,4 , 0,6 , 0,8 i 1,0) pripremljenih uobičajenom keramičkom tehnikom, izvršena su mjerenja difrakcijom rendgenskog zračenja, diferencijalna termička analiza, optička mjerenja u infracrvenom području i snimanja skanirajućim elektronskim mikroskopom. Analiza difrakcije rendgenskog zračenja indicira da uzorci imaju jednu fazu sa spinelnom kubičnom strukturom. Nadeno je da konstanta rešetke, promjeri tetrahedralnih iona, volumna i teoretska gustoća padaju a poroznost raste s porastom sadržaja nikla. Slike dobivene skanirajućim elektronskim mikroskopom indiciraju primjetne promjene među različitim smjesama. Spektri infracrvene apsorpcije pokazuju četiri karakteristična vrha za ferite. Položaj i intenzitet vrhova značajno ovise o sastavu sistema