CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
Neutron irradiation effects in different tungsten microstructures
Authors
D. Papadakis Dellis, S. Chatzikos, V. Manios, E. Stamatelatos, I.E. Messoloras, S. Mergia, K.
Publication date
1 January 2021
Publisher
Abstract
In this work the correlation of the neutron radiation damage and tungsten (W) microstructure is investigated. Further, the modification of the structure as a result of the neutron irradiation is assessed and its effect on the mechanical properties is determined. Forged bar (ITER grade), cold rolled sheet, and single crystalline tungsten materials were neutron irradiated at 600 °C to a damage of 0.12 displacements per atom. Neutron irradiation results in the formation of voids of almost the same size (larger than 1 nm) and dislocations detected by positron annihilation lifetime spectroscopy. All W grades have similar total dislocation densities, in the range of (1.6-2.4)×1014 m-2, as determined by electrical resistivity measurements. After irradiation the hardness of all tungsten grades increases and the largest increase is that of the single crystal (47%), whereas the smallest that of the sheet (13%). Increase in the yield strength, correlated to the increase of the hardness, is also found. The largest increase is observed for the single crystal (25%) and the smallest for the sheet (6%). The different degrees of hardening and strengthening indicate that the microstructure of the different tungsten grades has a significant influence on their neutron radiation damage resistance. © 2021 IOP Publishing Ltd
Similar works
Full text
Available Versions
Pergamos : Unified Institutional Repository / Digital Library Platform of the National and Kapodistrian University of Athens
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:lib.uoa.gr:uoadl:3023998
Last time updated on 10/02/2023