The measurements of the superconducting transition temperatures Tc and the resistivity variation, Including the room temperature coefficient of resistivity α = (d ln ρ/dT)273, have been made for three binary Zr-3d (3d=Co, Ni or Cu) amorphous alloy systems and a number of ternary Zr2(Ni100−xMx)1 amorphous alloys (M=Ti, V, Cr, Mn, Fe, Co or Cu). In binary alloys, Tc decreases with decreasing Zr-content in agreement with the results of the photoemission studies and heat capacity measurements. However, the proportionality between the electron-phonon coupling constant λ (deduced from Tc) and dρ/dT predicted by the Ziman model is not generally valid. The variation of Tc and α in ternary alloys are strongly affected by the magnetic correlations for M = Cr and Mn. The observed α < 0 for all alloys can be qualitatively explained in terms of incipient electron localization.Mjereni su temperatura supravodljivog prijelaza Tc i promjena električnog otpora s temperaturom kao i temperaturni koeficijent električnog otpora na sobnoj temperaturi α = (d ln ρ/dT)273 za tri binarna Zr-3d (3d = Co, Ni ili Cu) staklasta sistema i za niz Zr2(Ni100−xMx)1 staklastih slitina (M = Ti, V, Cr, Mn, Fe, Co ili Cu). U binarnim se slitinama Tc smanjuje sa smanjenjem Zr i to je potpuno u skladu s rezultatima eksperimenata fotoemisije i mjerenja toplinskog kapaciteta dobivenim na sličnim slitinama, koji pokazuju da se elektronska gustoća stanja na Fermijevoj razini smanjuje sa smanjenjem količine Zr. Proporcionalnost između konstante elektron–fonon interakcije λ (izračunate iz Tc) i dρ/dT, kako to predviđa Zimanov model, općenito ne vrijedi. Promjene Tc i α u ternarnim slitinama za slitine s M = Cr i Mn pod jakim su utjecajem magnetskih efekata. Uočene α < 0 za sve slitine mogu se kvalitativno objasniti efektom početne lokalizacije elektrona