Odporność na scieranie aluminiowanych taśm stalowych

Abstract

The results of the abrasion resistance measurements of aluminized steel strips are presented in the hereby paper. Steel strips of DX52D+AS120 grade, before and after a heat treatment at temperatures of 200-1000 C for 1 – 5760 minutes, were tested. Tests of the abrasion resistance were carried on in a specially built device: rotating disk – sample performing a plane-rotary motion, with an application of a lubricating medium. Examinations of the abrasion resistance were also performed by means of the block-on-ring tester. Estimations of a coating mass loss, roughness and thickness changes were carried on. The obtained results are illustrated by diagrams and macro- and micro-observations. Phase analysis investigations were also performed on samples selected after the abrasibility testing. The range of the heat treatment parameters – after which the Al-Si coating increased its abrasion resistance – was estimated.W artykule przedstawiono wyniki badan odpornosci na ścieranie aluminiowanych tasm stalowych. Badaniom poddano taśmy stalowe z gatunku DX52D+AS120 przed i po obróbce cieplnej w temperaturze 200-1000 C w czasie 1min-5760min. Wykonano badania odporności na ścieranie w specjalnie przygotowanym urzadzeniu typu obracająca się tarcza – próbka, wykonujaca ruch posuwisto-zwrotny, przy zastosowaniu środka smarujacego Zrealizowano także badania odporności na zużycie cierne za pomocą testera typu rolka-klocek. Dokonano oceny ubytku masy, zmian chropowatoąci i grubości powłoki. Wyniki badan zobrazowano za pomocą wykresów oraz makro i mikro obserwacji. Przeprowadzono także badania analizy fazowej na próbkach wytypowanych po badaniach ścieralności. Określono taki zakres parametrów obróbki cieplnej, po której następuje wzrost odporności na ścieranie powłoki Al-Si