The Stress Corrosion Cracking (SCC) initiation in filler metal (FM) 82 was studied in oxygenated (O2) water at 288 °C. Post-test microstructural characterization revealed that cracked grain boundaries (GBs) always exhibited a porous oxide incursion. Some intergranular (IG) cracks exhibited an oxide along the crack walls, which appeared to form after the crack advanced. Furthermore, similar porous oxide incursions were observed at the GBs on the non-stressed FM 82 coupon after oxidizing for a similar duration. The formation of oxide incursions is discussed, and the evolution of crack initiation is proposed

The University of Manchester - Institutional Repository

Stress corrosion crack initiation in filler metal 82 in oxygenated high-temperature water

https://pure.manchester.ac.uk/ws/files/254009631/AAM_Nic_Cor._Sci_1.docx

Stress corrosion crack initiation in filler metal 82 in oxygenated high-temperature water

Abstract

Similar works

Full text

Available Versions

The University of Manchester - Institutional Repository