In this study, we focused on the elongational rheology and the morphology of an electrically conductive polycarbonate/multiwalled carbon nanotubes (2 wt%) composite in the melt. In shear and melt elongation, the influence of the carbon nanotubes was large when the externally applied stress was small. Consequently, the elastic interactions resulting from the carbon nanotubes dominated in the low frequency range of the shear oscillations. The elongational viscosity of the composite was only moderately influenced by the addition of 2wt% carbon nanotubes. Transmission electron microscopy investigations of the stretched composite showed that isolated carbon nanotubes were oriented in elongation. In recovery after melt elongation, the recovered stretch of the composite was much smaller than the recovered stretch of pure polycarbonate. This effect is caused by the carbon nanotubes network, which prohibited large extensions of the macromolecules and led to a yield stress of the composit